Electronics Forum | Fri Feb 22 15:16:24 EST 2002 | rkevin
Bet your using tin/ lead plated components with a lead free Cu/Ag/Sn alloy. It leads to intermetallic cracking. Wow didn't anyone tell you to check the archives yet, It seems to be the answer given to everyone. Why have an interactive site if you alw
Electronics Forum | Thu Oct 01 09:58:30 EDT 1998 | Jacqueline Coia
Could you tell me please when the lead free solder regulation will become mandatory in Europe and also what are the current industrial alternatives for paste, bar and wire. Cheers, Jack
Electronics Forum | Wed Oct 07 15:44:43 EDT 1998 | CW
There's a good article on lead-free assembly of mixed technology in the May issue of SMT Magazine (pg. 52)
Electronics Forum | Thu Feb 16 12:41:50 EST 2006 | fredericksr
Hey folks, I was interested in any information that you might have on tombstone reduction when using a lead free solder and profile. Thanks for any input that you may have! -Russ #x
Electronics Forum | Wed Jan 28 21:47:56 EST 2009 | padawanlinuxero
Hello! I am having trouble with the new changes from lead joint to lead free joint, we are working on change to lead free, I am using a 3 zone oven reflow, the zone temps are : zone 1 zone 2 zone 3 (top and bottom) 128 208 260 th
Electronics Forum | Tue Oct 21 23:28:59 EDT 2003 | xz xiao
We all know the Lead Free process is trend, so we trial run it, now it is only my comment that we have a good achievement after several tries,we have taken serveral photos about Lead Free process with ErsaScope. 1.The surface of the solder joint are
Electronics Forum | Tue Oct 21 23:29:08 EDT 2003 | xz xiao
We all know the Lead Free process is trend, so we trial run it, now it is only my comment that we have a good achievement after several tries,we have taken serveral photos about Lead Free process with ErsaScope. 1.The surface of the solder joint are
Electronics Forum | Tue May 31 16:47:51 EDT 2005 | George
Dump the pot and put in the SN100C. Don't mix, too much tin.
Electronics Forum | Wed Nov 02 11:25:46 EST 2005 | dougm
I should specify that I am using SAC 305 as well.