Electronics Forum | Wed Dec 09 03:34:06 EST 2009 | cunningham
Sorry i wasnt very clear we already have a Malcolm sps-1 for our tubs but to move over to cartridges we need a machine to do that none of those machines are capable of mixing a 6 oz cartridge
Electronics Forum | Wed Jul 27 10:07:16 EDT 2011 | swag
We bought air dispenser guns that fit the cartriges. I can't remember where we got them - sorry. We built little aluminum "holsters" for the sides of the machines to put the guns in. The guns are hooked up to air with low pressure regulators. Wor
Electronics Forum | Thu Jul 28 07:23:24 EDT 2011 | scottp
My group supports a couple hundred lines all over the world. Most of them use squeegees but a few use either the MPM Rheometric pump heads or the DEK Proflow heads. I absolutely hate the enclosed heads. Flux separation, compaction, and the print q
Electronics Forum | Thu Sep 23 08:08:12 EDT 2021 | SN
Hi. Anyone in this forum experienced the lead-free solder paste SAC305 and SAC405? What are the differences to expect for solder paste with SAC305 and SAC405? What is the effect of silver (Ag) alloy in solder paste? It was really appreciated if could
Electronics Forum | Thu Jun 28 09:54:06 EDT 2012 | mosborne1
Dave, They rework fine. All solder joints on the whole board look great especially for lead free sac305. Here are the reflow specs: SAC305 no clean solder paste – Kester EM907 Kic thermal profiling device – 50%process window green light profile. • M
Electronics Forum | Tue Nov 21 12:35:59 EST 2006 | CK the Flip
It probably depends on the Silver content. We are also using Sn62Pb36Ag2. The paste manufacturer told us that the reason for the small silver content was so that it could wet better to the lead-free component and board finishes bearing silver.
Electronics Forum | Wed Jan 07 14:33:00 EST 2015 | eezday
The assumption that a HASL Sn63 PCB can be soldered with SAC solder paste is likely a bad one. The board itself is likely FR4 which can be damaged by lead free temperatures. The HASL finish isn't an issue from the perspective of it's makeup and actu
Electronics Forum | Fri Feb 23 14:51:48 EST 2024 | carl_p
Just another thought - how long is the printer idle for between boards? is it long enough to have the chemicals start to separate within the paste?
Electronics Forum | Fri Nov 17 14:42:06 EST 2006 | billwestiet
Mark, This is a big topic. Where are you located, it would probably be best to hook you up with someone in your area. Anyhow, lead or lead free should be based on whether the circuits are lead or lead free. I would guess that cell phones would all
Electronics Forum | Wed Jan 07 15:48:22 EST 2015 | jacklucas
We switched our PCB's to 170Tg over 10 years ago, so we're probably good to go on the temperature aspect. Thanks for the opinion on the added lead content.