Electronics Forum | Mon Feb 05 11:31:37 EST 2007 | davef
While you're waiting for others to reply, look here: http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=19507
Electronics Forum | Wed May 21 13:59:19 EDT 2008 | pjc
Here's what I've seen for no-clean flux applications: Leaded: Dwell Time is? 2 - 3 seconds Top side board temp max? If some small SMT parts reflow are we too hot? 110 to 120C top side board temp just before hitting the wave(s) Pot temp. 245C Lea
Electronics Forum | Fri Feb 19 14:43:46 EST 1999 | Nithy
We are in the process of getting into no-clean paste and fluxes. One important issue in this is sodler balling. I have heard some people say that having a matte finish would help in having lesser solder balls and that the solder balls would not be
Electronics Forum | Tue Nov 02 05:00:28 EST 2004 | jysam
we are using solder paste WS609 and OM5100.Relow oven: forced convection type. For WS609 and OM5100, straight ramp up profile is suitable for low to medium thermal mass assemblies and preheating may be required for high thermal mass assemblies. How
Electronics Forum | Thu May 13 20:40:25 EDT 2021 | winston_one
Yes, we can't use pure Pb PROCESS. And as I say we will not use it anyway, as we have lead-free BGA's, LGAs, component with Solder Charged Terminations... It's became almost normal practice to solder it with leaded solder pastes. In this case peak re
Electronics Forum | Mon Jan 15 09:19:29 EST 2007 | tk380514
We use Alpha EF-2202 low-VOC No-Clean flux Selective wave soldering cassettes Bottom pre-heating wave soldering machine We have one component that will not solder properly: http://www.epcos.com/web/generator/Web/Sections/ProductCatalog/Capacitors/Ul
Electronics Forum | Mon Dec 17 11:55:08 EST 2007 | chef
I recently had the same problems, solder bridges on every thing I made, different customers boards, etc. I wave with no-clean flux. As I sorted out problems (pin holes, blow holes, splatter, etc.) I found a lot of variable factors. I changed flux,
Electronics Forum | Mon Feb 05 09:48:51 EST 2007 | George
Good morning, What is considered "high frequency" ,.i.e. Mhz,GHz,etc., when we talk about possible issues with NO-clean flux residues and product's application? I appreciate your help on this... Have a good one! George
Electronics Forum | Tue Feb 23 12:56:03 EST 2010 | vleasher
Is there any harm in washing SMT soldered with NoClean paste? The PCA has some large thru-hole connectors that we would prefer to do as water soluble on out selective solder but the SMT consists of LGA's and other low parts that we would not be able
Electronics Forum | Fri Jan 28 01:56:32 EST 2005 | Chua
Hi, I could like to find out what are the things need to look out if I'm doing a new SMT solder paste ( water soluble & no-clean ) evaluation. And also flux ( spray type ) for wave-solder ( water soluble & no-clean ). Appreciate for all the input..