Electronics Forum | Wed May 27 14:35:52 EDT 1998 | Justin Medernach
| | R&D is currently designing a board with smt components on both sides of the board. They are adding a 16 pin IC Gull wing. on the bottom side of the board. I have asked for only caps and resistors to be placed on the bottom side. Is there a recomm
Electronics Forum | Wed May 27 13:42:08 EDT 1998 | Chrys
| R&D is currently designing a board with smt components on both sides of the board. They are adding a 16 pin IC Gull wing. on the bottom side of the board. I have asked for only caps and resistors to be placed on the bottom side. Is there a recommen
Electronics Forum | Sat Jun 12 19:48:47 EDT 2010 | bootstrap
I like what you're doing. 20 years ago anyone, hobbyists and tiny garage-shop companies could create electronics devices just as sophisticated and cool as big corporations. Today, SMT has largely trashed the creativity (and competition) that existe
Electronics Forum | Wed Jul 14 21:34:16 EDT 1999 | karlin
| | | | | Hi, | | | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | |
Electronics Forum | Tue Jul 13 14:19:00 EDT 1999 | JohnW
| | | Hi, | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | | | | | | Sec
Electronics Forum | Tue Jul 13 14:25:57 EDT 1999 | Earl Moon
| | | | Hi, | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants) | | | | |
Electronics Forum | Thu Jul 15 14:38:38 EDT 1999 | JohnW
| | | | | | Hi, | | | | | | | | | | | | I need some urgent informations on stencil design guidelines on how to perform epoxy printing on 0603 and 0402 components. Could anyone help? ( Reflow process is not possible because of some other constriants)
Electronics Forum | Wed Dec 26 14:21:47 EST 2007 | gersla
I am looking for suggestion of BGA 0.5mm pitch Ball 0.3mm (BGA 8x8mm)assembly and soldering. Stencil thickness? Stencil reduce? Etc.
Electronics Forum | Fri Mar 09 05:06:09 EST 2012 | grahamcooper22
Is your solder paste deposit drying out? Or if the paste deposit is small or there is insufficient paste then the tack between the device and paste will be poor so it can easily come out of the paste during its placement or placement of other parts.
Electronics Forum | Fri Oct 22 21:23:59 EDT 1999 | se
Tombstoning is usually oven profiling, see October 14 thread below. Aperture rules are misleading. Component mix, stencil thickness, paste factors, all contribute. Also, are you making the stencil from a paste or pad layer or from a soldermask layer?