Electronics Forum | Wed Nov 22 02:37:20 EST 2006 | brodalvin
Thanks a lot for the responses...��
Electronics Forum | Tue Jan 23 17:21:30 EST 2007 | russ
Which characteristics? Russ
Electronics Forum | Mon Mar 22 19:46:17 EST 2004 | pdeuel
The bottom side is going into reflow somewhare near melting point of solder. Reduce bottom side temprature. Get a good mole so ramp and soak tempratures can be checked on bolth sides of the PCB. The object is to keep bottom side parts from approching
Electronics Forum | Mon Nov 20 21:55:21 EST 2006 | brodalvin
Does SnPbAg solder paste have a reliability risk if subjected 2 times in reflow oven at 230�C? I want to implement my project immediately. If samples will be subjected to our reliability it would take three months before I can implement my project.
Electronics Forum | Thu May 05 01:21:42 EDT 2011 | city4497s
Hi Davef The problem shows up on * random location including component pads * all PCB and different PCB supplier * different solder paste lot * both printing and dispensing process * all production shift * we have only 1 production line It black,
Electronics Forum | Tue Apr 27 08:14:59 EDT 2004 | iqbal
Is anybody doing BGA soldering water clean solder. If yes how you are ensure cleaness. We have boards with Four BGA and 2000 chip and ICs.We are processing with no clean solder but we are getting bad wetting so now we are planning to switch to water
Electronics Forum | Tue Mar 01 11:19:47 EST 2011 | jeddmartens
I have no knowledge into PCB designing with surface mount components, all my experience has been with through hole components. I now have to design PCBs using surface mount parts. I have a few questions I was hoping someone could answer. Can a PCB w
Electronics Forum | Tue Jan 23 16:22:01 EST 2007 | asir
I'm looking for a PbF solder paste with similar characteristic as the 63/37Pb alloy. What alloy composition would you recommend?
Electronics Forum | Fri Oct 18 00:44:56 EDT 2019 | Aqueous Technologies
I know you mentioned you use a Tech Spray product. We have had success with their "Wondermask" water soluble product. When using a chemical additive (saponifier) in an aqueous cleaning system we have not experienced residues. I hope that helps. https
Electronics Forum | Tue Nov 21 09:46:19 EST 2006 | jax
I assume you are talking about Sn62Pb36Ag2 solder. You should not see any added concerns when subjecting Sn62 to multiple reflow cycles as compared to Sn63. As compared to Sn63Pb37: Reduced leaching issues Increased Wetting due to lo