Electronics Forum | Fri Jun 18 03:31:38 EDT 1999 | Frank
| | Hello, | | I am looking for the surface resistivity and volume resistivity of standard fr4 as a function of temperature and /or humidity . can any one help? | | | | Frank: Sorry I'm so late getting back to you. | | 1 Use either ASTM D5109-
Electronics Forum | Thu Oct 02 17:54:46 EDT 2003 | davef
Yes, Russ IPC-6012A w A#1 - Qualification & Performance For Rigid Printed Boards talks to solder mask requirements in 3.8. One interpretation of what it says: * Solder resist [solder mask] must meet the qualification / conformance requirements of S
Electronics Forum | Tue Feb 27 22:40:28 EST 2007 | davef
IPC-A-600G, 2.9 Solder Resist [Solder Mask] [snip]"Solder resists are used to limit and control the application of solder to selected areas of the printed circuit board during assembly soldering operations and are sometimes used to reduce dendritic f
Electronics Forum | Fri May 25 13:24:38 EDT 2007 | mfgengr
I had a similar problem a long time ago. I eventually traced the problem to undercured solder resist. The flux was reacting with what was left of the uncured resist, leaving a white residue. We could not even hand scrub this off. The solution was to
Electronics Forum | Mon Jan 14 06:28:18 EST 2008 | gregoryyork
Hi its normally down to the state of cure of the resist type not the actual type be it matt or gloss. If its not cured correctly it will produce solder balls. Pending where you are you could try our 35-41 or new 35-41-30 flux this will reduce the pro
Electronics Forum | Thu Jan 15 03:20:59 EST 2009 | sachu_70
Hi Andrzej, I guess you mean peelable solder resist. Good idea to try during R&D, but certainly not a solution on production floor. Also, few constraints to be considered such as presence of entrapped air between component and solder resist, the natu
Electronics Forum | Thu Feb 17 02:49:04 EST 2000 | Roni Haviv
Hi, I need a wear resistance PCB finishing over bare copper (If exist!), the surface have a moving part which slides over it and bare copper as a surface is not good enough. I'll apprechiate any information. Thanks Roni
Electronics Forum | Fri Aug 11 10:47:51 EDT 2000 | Peter Curtis
Does anybody have any information regarding the plus's and minus's of both copper and solder resist defined lands?
Electronics Forum | Thu Feb 17 02:49:04 EST 2000 | Roni Haviv
Hi, I need a wear resistance PCB finishing over bare copper (If exist!), the surface have a moving part which slides over it and bare copper as a surface is not good enough. I'll apprechiate any information. Thanks Roni
Electronics Forum | Mon Jun 14 11:19:48 EDT 1999 | Frank Frimpong
Hello, I am looking for the surface resistivity and volume resistivity of standard fr4 as a function of temperature and /or humidity . can any one help?