Electronics Forum | Thu Oct 07 15:39:59 EDT 1999 | Carol Zhang
| I have a board, 4 spacers needed to be soldered on the board | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there will b
Electronics Forum | Fri Oct 08 08:26:03 EDT 1999 | Carol Zhang
| | | I have a board, 4 spacers needed to be soldered on the board | | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, ther
Electronics Forum | Tue Oct 12 08:48:16 EDT 1999 | Carol Zhang
| | I have a board, 4 spacers needed to be soldered on the board | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there wi
Electronics Forum | Fri Oct 08 16:48:57 EDT 1999 | Dave F
| I have a board, 4 spacers needed to be soldered on the board | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there will b
Electronics Forum | Fri Oct 08 10:08:48 EDT 1999 | Glenn Robertson
| | | | I have a board, 4 spacers needed to be soldered on the board | | | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first,
Electronics Forum | Thu Oct 07 16:57:02 EDT 1999 | Glenn Robertson
| | I have a board, 4 spacers needed to be soldered on the board | | first with the normal 62Sn37Pb alloy. Then, capacitors are manually soldered on the boards. The density of the board is quite high. If we wave soldered capacitors first, there wi
Electronics Forum | Wed Jan 17 07:28:29 EST 2007 | davef
Look here: http://www.smtinfo.net/Db/_Reflow%20Soldering.html
Electronics Forum | Wed Jan 07 17:39:26 EST 2015 | duchoang
Additional info: I use SAC305 solder paste on Enig PCB.
Electronics Forum | Thu Jan 08 15:49:10 EST 2015 | emeto
I bet you that the problem comes from the ENIG brittle solder joints. About low temperatures I think you can go to the absolute 0 and the device should still work.
Electronics Forum | Mon Nov 15 21:32:31 EST 1999 | Dave F
Wolfgang: Sounds like gluteus maximus protection time. 1 "Maximum suitable temperature for the solder joint should be half the liquidous temperature" is a good rule of thumb. Where it came from, I don�t know. One place I�ve seen it repeated is: H
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830
.gif)