Electronics Forum | Mon Sep 28 19:07:47 EDT 1998 | Steve Gregory
| I have had some field failures returned recently, the boards had flux contamination under the components in a sensitive area, Nothing really visible until the component was removed, and the board had no evidence of rework of any type. Is it poss
Electronics Forum | Wed Jul 21 17:49:52 EDT 2004 | jsk
problem: Too many solvents and boards are not clean Flux remains on the board after vapor degreaser and "Powdery" white residue after vapor degreasing Flux type is kester 186 Process: hand solder High Temp alloy, spot clean after hand solder e
Electronics Forum | Thu Sep 06 10:34:21 EDT 2001 | Mike Konrad
Hi Jeff, Sean is correct. Although ultrasonic technology will work in post-reflow de-fluxing applications, you will receive concerns regarding ultrasonic �damage� to wire bonded components. Much has been written to combat this belief but the conce
Electronics Forum | Thu Mar 17 03:07:17 EST 2005 | Chua
Hi, We are running lead free at wave solder now and the spray flux system is down. If we are going to able the flux manually, what problem will we be facing with the excess flux able. Appreciate for the advise.
Electronics Forum | Mon Nov 12 12:59:19 EST 2007 | ck_the_flip
Here are the scenarios: *No-Clean Flux & Foam Fluxer: alcohol is used as a thinner (for titration purposes) if your flux is alcohol-based *No-Clean Flux & Spray Fluxer: alchol is used only as a cleaning agent for your sprayhead.
Electronics Forum | Fri Jan 28 01:56:32 EST 2005 | Chua
Hi, I could like to find out what are the things need to look out if I'm doing a new SMT solder paste ( water soluble & no-clean ) evaluation. And also flux ( spray type ) for wave-solder ( water soluble & no-clean ). Appreciate for all the input..
Electronics Forum | Wed Apr 19 04:41:42 EDT 2006 | ge_lim
Hi I am using selective soldering to dip soldering the connector pins to the PCB and would like to know your experience: a) Is there a recommended dip or dwell time for the dip soldering? b) How do we improve the solder coverage in the TH? c) How t
Electronics Forum | Tue Jul 06 14:23:27 EDT 1999 | Earl Moon
| | | I've heard that use of VOC free flux with wavesolder fixtures can be challenging due to entrapment of water in the fixture. | | | | | | Is anyone out there successfully running VOC free with wave fixtures & did you experience problems? If so,
Electronics Forum | Wed Feb 26 23:59:48 EST 2003 | Mike Konrad
Grant, No-Clean paste + IPA = White Residue! #1: Stop using IPA #2: Switch to either a solvent-based de-fluxing chemical or an aqueous-based de-fluxing chemical. If you are using an ultrasonic cleaner for your boards as stated, do not use sapon
Electronics Forum | Thu Jul 22 17:26:16 EDT 2021 | proceng1
Spray or foam? Are you looking for IPA or Water based?