Electronics Forum | Fri Jun 12 11:15:50 EDT 1998 | Ryan Jennens
Hey all! The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is on a pallet w
Electronics Forum | Wed Jul 05 09:00:13 EDT 2006 | russ
Sounds like possibly too little preheat. Russ
Electronics Forum | Mon Jun 12 10:57:51 EDT 2000 | Jason
I am new to wave soldering. Any information is greatly welcomed. Here is the problem. After soldering the boards they have a film on the bottom of them and sometimes a white powder looking substance. I have tried decreasing the amount of flux on
Electronics Forum | Wed Jul 05 13:30:37 EDT 2006 | Chris Griffin
Likely causes of this are: -Preheat temp. too low -too much dross -uncured epoxy -PCB contamination ...also varify the solder flow over the wave is smooth.
Electronics Forum | Thu Jul 06 04:41:58 EDT 2006 | Rob
MF300S is quite an old flux, & a lot has happened since then on the flow solder front - are you sure it's designed for Lead free, or is it just a traditional flux that SHOULD work OK with Lead free?
Electronics Forum | Wed Jul 05 10:13:02 EDT 2006 | jdengler
Is the flux rated for lead free? These higher temps will cause most lead rated fluxes to burn off prior to the wave. Jerry
Electronics Forum | Thu Jul 06 12:26:55 EDT 2006 | Chunks
Sounds like your flux to me. Since you cannot change the board or the machine, changing flux would be one question mark you could take away with a phone call and a sample. You will really be surprised how different fluxes can affect your final prod
Electronics Forum | Mon Jul 10 07:46:51 EDT 2006 | ronalds
You are right, RSS profile is not the correct description. I am using a profile which heats up quickly to let the flux spread. Next linear up to activate the flux and prevent thermoshock. My experience is however, that small changes in this profile
Electronics Forum | Mon Jul 03 05:39:05 EDT 2006 | ronalds
Hi, I am experience problems while testing wave soldering SMT components that are glued on the solderside (lead free). Between de leads of SOx type IC's and SOT's develop a great deal of solder beads. I have been using a RSS temp.profile while spr
Electronics Forum | Thu Jul 06 12:52:35 EDT 2006 | samir
..and he can put the flux in and keep it a secret too from his customer.. RSS profile on wave?? I never heard of a soak zone for wave preheat...you may be burning off your activator..hence, the beads. For wave preheat, your main goal is to ramp up