Electronics Forum | Tue Dec 10 14:10:38 EST 2002 | Randy Villeneuve
Steve, I wave solder most if not all our boards with selective wave pallets. I did not catch if the solder balls were on top of the board or on the bottom but that will make a difference on what to do to get rid of them. Pallets are good and bad. On
Electronics Forum | Thu Feb 04 09:09:07 EST 1999 | dave
Can anyone help me with the pros and cons of trying to wave solder tantalum and large (1812) ceramic capacitors. I do know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what problems I c
Electronics Forum | Fri Feb 05 09:39:58 EST 1999 | Dave F
| Can anyone help me with the pros and cons of trying to wave | solder tantalum and large (1812) ceramic capacitors. I do | know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what proble
Electronics Forum | Tue Feb 16 16:28:30 EST 1999 | Tuffty
| | Can anyone help me with the pros and cons of trying to wave | | solder tantalum and large (1812) ceramic capacitors. I do | | know that one may see fractures on larger cermaic caps, but have not seen much on the tantalums. Any insight as to what
Electronics Forum | Mon Nov 21 06:49:57 EST 2005 | pjc
Go to this link for a nice tool for wave solder process troubleshooting: http://www.speedlinetech.com/news_publications/application-notes.aspx?OnId=5 Look for "Wave Solder Troubleshooting Wizard" If you have an Electrovert machine, contact applica
Electronics Forum | Thu Nov 17 13:13:49 EST 2005 | Mike
Hello, Some questions.... Are you running lead free? What alloy? What�s your pot temp at? Temp of the board after preheat? Are you getting any solder in the barrels (
Electronics Forum | Thu Nov 17 20:23:14 EST 2005 | cangly
Hi Russ, We control the gravity of flux each 8 hours and will mix thinner to balance it if any.. Do we need more any action for this.. Thanks for your advices.
Electronics Forum | Fri Nov 18 08:31:09 EST 2005 | jdengler
This is way too long of a time. The SG probably changes significantly over this time. This could be a major contributor to your problems. Jerry
Electronics Forum | Thu Nov 17 03:34:51 EST 2005 | cangly
Hi, We have a board with over 100 chips (mixed size) and some long Connector DIP through out Wave solder with many issues of no solder and solder bridge, (using clean flux with bubble fluxer and Kester solder bar). Currently we tried to reduce the de