Electronics Forum | Wed Aug 02 12:04:42 EDT 2017 | davejohnson
Hopefully not too late of a reply... We currently have both, the Ersa ETS 330 (running LEAD solder) and Seho GoWave 1030 (RoHS solder). Bought the Ersa used, and it seems like a strong built industrial high volume machine. We've needed to modify it a
Electronics Forum | Fri Jun 12 15:56:43 EDT 1998 | Ryan
| | | Hey all! | | | The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is o
Electronics Forum | Fri Jun 12 14:31:04 EDT 1998 | Earl Moon
| | Hey all! | | The wave solder warrior is back. I have found a flux which leave almost no residue (the least yet), but because of its super low solids content I absolutely cannot get topside fillets. The multi-layer, two sided board is on a
Electronics Forum | Mon May 07 22:28:17 EDT 2007 | colormaker
radiant heat. 137c The hollis was a great machine. The one I had the prehead wass on or off there was no setting. The pot temperature guage was brocken so I had to guess and manually turn the heater on and off. The whole machine was covered with 1 i
Electronics Forum | Thu Nov 20 18:57:52 EST 2014 | warwolf
I can only say it looks okay for what you need, you will want a dual wave system it can make things so much easier. One thing to check would be the wave nozzle sizes I can see that the conveyor will do up to 15" but thats not to say the nozzle is
Electronics Forum | Mon Feb 13 13:26:21 EST 2006 | pjc
If you're asking about wave solder machine, yes you can run Sn/Pb in a "Pb Free" machine. The concern is that when its time to run Pb Free you're going to have to remove all the parts from the solder pot to remove all the Pn/Pb solder residue from po
Electronics Forum | Sat Jan 29 16:35:33 EST 2000 | Robert Steltman
We have a Seho wave soldering machine and cannot seem to get rid of dross that is being generated within the solder pot, and is being pumped out in the wave. It is not the same kind of dross that forms on the surface of the solder pot(this is very m
Electronics Forum | Thu Aug 31 11:34:44 EDT 2006 | flipit
Could you get by using a Wenesco or Air Vac PCBRM10 wave pot instead of an entire wave soldering machine?
Electronics Forum | Tue Feb 14 03:58:17 EST 2006 | Rob
Yes, it's fine - as Pete says you have to replace certain parts & either get the pot recoated or a new one. We ran a "Lead free" 6622C from Vitronics Soltec on Tin Lead, then it was cleaned up, recoated and loaded with a no-lead alloy with no proble
Electronics Forum | Tue May 26 06:56:40 EDT 2009 | xinxi
Hi! From your post, it seem like the wave did not really touch the component. You probably need to get the both wave height correct and that it hits the component.It is normal for solder to come through the PCB when using chip wave. The through-hole