Electronics Forum | Tue Mar 08 09:56:05 EST 2005 | caldon
Tim- You have two separate issues 1) Stencils and 2) wave. Stencils you can purchase a ultrasonic system that will remove the paste automatically or you can use stencil wipes to remove it manually. I would refrain from using towels and IPA as it dilu
Electronics Forum | Fri Apr 29 07:29:58 EDT 2005 | siverts
Steve, Thanks for Your replay and I agree with You. But sometimes I find it hard to always have the optimum in every aspect of our high mix/low volume electronics assembly production. We also do a lot of prototype production. In this case we had to g
Electronics Forum | Tue May 24 19:35:36 EDT 2005 | davef
Certainly, most often, the focus of pot analysis is directed at controlling impurities. Maintaining proper level of tin is important, also. When the portion of tin decreases: * Liquidous temperature increases. * Ability to wet decreases. * Solder c
Electronics Forum | Sat May 28 06:40:24 EDT 2005 | steve
Aim offers excellent soldering fluxes. That said your probably dealing with the local representative. The FIRST question to ask when evaluating any chemistry is "What is the Availability of the flux". Distributors don't necessarily stock all of a man
Electronics Forum | Thu Sep 08 06:19:55 EDT 2005 | lupo
Hello, Could anyone provide some support concern issue with vertical fill of through hole solder. Our lead free wave soldering process is not capable to fill 100% (requirement of our customer)through hole. We made everything (DoE) - different amoun
Electronics Forum | Tue Dec 27 07:22:44 EST 2005 | davef
It could be lots of things. You're not helping to narrow those alternatives. So, consider taking a sample to: * An analytical laboratory. * Teachers in the chemistry department at a local university. Kester recommends the following independent la
Electronics Forum | Thu Jan 05 20:34:32 EST 2006 | davef
We agree. It sounds like your tester is possessed. If it starts vomiting pea soup, throw it away. Otherwise: * Follow Pete's suggestion by calling Alphametals [or whatever they call themselves nowadays] * Contact analytical laboratories and ask th
Electronics Forum | Thu Feb 16 13:21:24 EST 2006 | Bill C
Hi Russ, Thanks for the reply. No this is 856, I sprayed some on boards just to try it out and noticed it dries very quickly also but if its soldered right away as would be the case in the machine, it's fine. I believe I tried some 857 and found th
Electronics Forum | Fri Mar 17 10:16:10 EST 2006 | Chunks In Cebu
Just thought of something while on the beach. We made a paste change several years ago when we installed another surface mount line. At around that same time, our maint. crew changed chain oil and about 2 months later changed when they oiled the ch
Electronics Forum | Wed May 10 00:27:46 EDT 2006 | Chris
Russ, By a longer profile you mean a more even slope across the entire profile. Unfortunately I only have a 5 zone oven that is fairly short. How many heated zones are you using? Did you shrink the 0402 pad design and leave less pad exposed out a