Electronics Forum | Tue Apr 13 18:11:00 EDT 1999 | Jimmy Strain
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Mon Apr 19 11:21:03 EDT 1999 | Travson
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Mon Apr 19 20:49:13 EDT 1999 | Dave F
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Mon Feb 22 14:30:55 EST 1999 | Steve Gregory
Hi Bill! Justin hit the nail on the head with his advice. One other thing I'd add too is that if your volume and such points to using cartridges, I found that sometimes operators can get a little wasteful. I worked for a memory company where we
Electronics Forum | Thu Jan 28 14:10:57 EST 1999 | Tom B
Hello Netters, I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI solder mask
Electronics Forum | Thu Jan 28 15:43:16 EST 1999 | Dave F
| Hello Netters, | | I need some info, Earl or Dave, I have a PCB that exhibits a white layer on solder side. It does not appear to be surface residues (IPA has no effect), but looks like its under solder mask. My first guess is that the LPI solde
Electronics Forum | Sat Jan 23 16:07:20 EST 1999 | Steve Gregory
| hi, | i am working towards developing a no-clean process for a customer at contract manufacturing facility. the assemblies have gold fingers on them. these are masked to prevent from any damage to them during reflow soldering. the earlier proces
Electronics Forum | Sat Oct 10 04:58:18 EDT 1998 | Tony B
| *Reply to: ericr@nj.tanon.com | | Without going into a lengthy explaination {at this time}, has anyone experimented, tested, evaluate, and/or 'perfected' an SMT double-side reflow process. Presently I'm using a Kester R593 OA (water soluble) Sn63/
Electronics Forum | Tue Sep 15 08:59:59 EDT 1998 | Chrys
| I am running composite fixtures on my wave solder machine and after about 500 passes each (1 month)they are showing serious signs of wear in that the composite surface is bubbling up and glass fibers are also starting to show. | The problem here
Electronics Forum | Fri Sep 11 17:23:00 EDT 1998 | Eric Miller
Hey Dave, sounds like your material is delaminating at a rapid rate, I would not recommend using them through your process, delaminating material has to go some where! When composite material is made, layers of fibre glass and epoxy resin are placed