Electronics Forum | Mon Jun 08 14:52:16 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Mon Jun 08 15:29:17 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Tue Jun 09 15:46:29 EDT 1998 | Aric Parr
| Hi there Gary, | Your solder ball problem is very similar the problem I experienced, but I was using a water soluble paste at the time. It started by inspectors telling me that they were seeing cold solder on some SIMM's that we had built regularly
Electronics Forum | Fri Feb 19 14:43:46 EST 1999 | Nithy
We are in the process of getting into no-clean paste and fluxes. One important issue in this is sodler balling. I have heard some people say that having a matte finish would help in having lesser solder balls and that the solder balls would not be
Electronics Forum | Wed Dec 09 18:51:06 EST 2020 | johndep7
My company has been having issues with a lot of solder balls, solder splash, and flux balls all over a specific board. Now this is one of the only companies that require us not to clean our boards after our work is finished but this is also causing a
Electronics Forum | Fri Jan 15 11:25:29 EST 1999 | E. R.
Does anyone have information pertaining to re-balling BGA components using balls that are preformed onto disolable paper waffers (mini BGA reballing kit)? The paper containing the specific BGA device/pattern would be placed onto the BGA then process
Electronics Forum | Wed Feb 18 12:42:43 EST 2004 | babe
OK, if the sphere of the ball and the paste on the pad are both eutectic, 63/37 then the paste will reflow first causing a drop of the component, after which the spheres will reflow causing a double drop and a good intermettalic. You can see this by
Electronics Forum | Fri Dec 11 08:56:08 EST 2020 | SMTA-64304223
One of the common causes of solder ballin is also outgassing from the boards have your tested the board for outgassing? Bob Willis
Electronics Forum | Tue Feb 17 04:52:13 EST 2004 | John W
There's normally a number of reasons people want to know what melts 1st, 1 - to see if you know, 2 voiding issues - whole can of worms 3 device alignment. One of our collegues has said that most balls are Eutectic, that's in fact not totally correct.
Electronics Forum | Fri Feb 27 11:33:32 EST 2004 | Bryan
Very strange question,but interesting.Is there anyone who have conducted any experiments to figure out the results?I made a profile board,one thermal couple on pad and other one drilled into the ball of BGA.the 2 points are perpendicular to conveyor