Well, im not sure what plane you guys are on, but I can back up my what im talking about. Ya see I wnet to Soltec traingin back in 1995 for our new wave. I got a diploma proofing that I know what i'm talking about. no one else in my company has on
Electronics Forum | Fri May 23 18:55:20 EDT 2008 | gregoryyork
This is one of the biggest mistakes with the Lead Free process. We have all listened to the 'industry experts' and followed their advice and unfortunately got it wrong. Keep the dwell times (dependant on alloy selection) the same as Leaded so you are
Electronics Forum | Tue Jan 31 15:51:04 EST 2006 | russ
Relays huh? I can tell you from previous experience that relays are not a good heat gun candidate. Did you check how long this part can withstand the 240? I do not know what the 4 setting is on a liester but it is probably well in excess of the 24
Electronics Forum | Wed Feb 10 05:23:17 EST 2021 | karl_willoughby
Hello. I am sourcing machines for an SMT line (for the first time) and would like to understand features of current and earlier model SPI and AOI machines. In the intended application, a high volume of PCAs aren't required to be processed but there
Electronics Forum | Sat Jul 24 00:04:55 EDT 1999 | Scott McKee
| | | There is a practise within the industry of an Inspector inspecting a board, and that same Inspector performing touch-up. My opinion is that the Inspection and Touch-up operations should be separate functions whereby the Inspector is not perform
Electronics Forum | Thu Sep 04 03:26:18 EDT 2014 | eurekadrytech
Hi all: Interesting question you have raised as it concerns the rate of absorption by the board material. I represent http://www.EurekaDrytech.com and could assist in resolving the blistering problems you're facing. First some questions. 1. Is the
Electronics Forum | Sun Sep 07 20:51:52 EDT 2014 | natashakt
1. Is the high RH environment consistently at 72% RH and 21.4 degrees Celsius? No, over the past 2 weeks I have recorded the highest at the moment: 67% RH at 22.6 degrees C and lowest (it is Spring not summer yet): 31.9% RH at 19.0 degrees C. Or d
Electronics Forum | Thu Apr 05 17:06:11 EDT 2018 | stephendo
We recently got a batch wash machine that can use a chemical cleaner. (not a saponifier). NOW I feel confident cleaning no clean boards. Without a machine that can heat water and use a proper cleaning agent, I would not trust cleaning no clean boards
Electronics Forum | Mon Dec 11 20:44:37 EST 2006 | davef
Title : LEAD-FREE WAVE SOLDER FLUX EVALUATION Author : Michael Havener Author Company : Benchmark Electronics, Inc Date : 09/25/2005 Conference : SMTA International Abstract : The European Union�s deadline to ban lead in electronic pr
Electronics Forum | Mon Mar 27 15:56:12 EDT 2017 | padawanlinuxero
Just 2 cents, lead free flux residue is no clean?, how about leaded flux? how much flux residue it leaves on both types? is there a clean up procedure after wave solder? or is there a wave solder process?