Electronics Forum | Mon Nov 07 16:34:55 EST 2005 | CW
If I am putting chip capacitors on a .063 FR4 board, what size package should we stay away from to avoid cracking? If I use 2 mil copper on the outside layers of a PCB, am I limited to what pitch of parts I can use? Specifically, will using 0603
Electronics Forum | Mon Nov 07 16:31:47 EST 2005 | CW
hi Bob, Thanks for the info. I understand your comments, but I am looking for specific guidance, If I am putting chip capacitors on a .063 FR4 board, what size package should we stay away from to avoid cracking? (I realize this is dependent on h
Electronics Forum | Tue Nov 15 16:07:39 EST 2022 | corusak
Hello everyone, I am working on a very low cost, small and basic vending machine ($300) with wooden cabinet for small neighborhood stores. As you may know, it is necessary to properly protect the components to prevent users from trying to steal money
Electronics Forum | Mon Jul 07 21:33:15 EDT 2014 | andrespena
The problem about covering it with glue (without using solder) is that the components might dislodge by a miniscule amount underneath the glue. So maybe the contact points will disconnect. I'm not sure if this will be a real problem, but if so it wo
Electronics Forum | Tue Nov 08 05:00:23 EST 2005 | rlackey
Hi CW, Regarding orientation, yes, your diagram is right - see the following link for confirmation. http://search.murata.co.jp/Ceramy/image/img/A18X/C2EB3C.PDF Regarding information on bending strength you want to talk to your local Murata office
Electronics Forum | Thu Jun 24 11:41:10 EDT 1999 | John Thorup
| Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody hel
Electronics Forum | Thu Jun 24 12:43:08 EDT 1999 | Earl Moon
| | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody h
Electronics Forum | Tue Aug 18 22:22:43 EDT 2009 | comatose
Assuming you want to run 8 hours a day and 5 days a week, you need a sustained throughput of 2.5k components per hour. With fine pitch, futzing around, setup, etc you should really look for machines rated in the 4k to 5k per hour range. That's not sc
Electronics Forum | Fri Jul 04 19:17:37 EDT 2014 | andrespena
Hi (I don't know if this forum is the best place to post something like this, but I don't know of other places on the internet, so... sorry if I'm in the wrong place) Might there be an easier way to add components (e.g. computer chips) to a circuit
Electronics Forum | Fri Jun 25 01:11:31 EDT 1999 | Vinesh Gandhi
| | | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody