Electronics Forum | Mon Jan 04 21:32:40 EST 2010 | boardhouse
Conductive Anodonic Filament My worry is that any extra moisture added to the Lead free Material during assembly may cause this Conductive filament to grow within the material weave. They are water washing after through hole assembly and then after
Electronics Forum | Tue Jan 05 18:19:40 EST 1999 | Dave F
| I'm looking for information on a company called AI Technologies. They make conductive adhesives and thermal management materials for attaching dice and heatsinks. Any feedback from users would be appreciated. Thanks, | | Chrys | Hey Chrys: I
Electronics Forum | Tue Dec 03 15:26:07 EST 2002 | GSW
This might be a trival mundane suggestion but try to use non conductive plate to hold components. Probably even made of the pallet material. I am sure your pallet fabricator will have tons of scrap and he can help you find one. T
Electronics Forum | Thu Dec 15 17:30:42 EST 2005 | GS
Yes Davef, storage condition and long time remaining on shelf could effect pealing strength, but we experimented that by using Polystirene Carrier Tape also this problem was reduced almost to zero. Df, If I am not wrong when you talk about pr
Electronics Forum | Tue Jun 21 17:27:10 EDT 2022 | kojotssss
Offcourse, RH is between 47-50%. The cause of problem is that the one of the embossed carrier reels/package materials coming from supplier static charged. Material now is like insulating, not dissipative or conductive. Example: https://drive.google.
Electronics Forum | Wed Apr 09 20:05:21 EDT 2003 | davef
Kevin: We know of no handy approach to developing recipes. * Certainly programs provided by profiler suppliers give you a good first pass, based on your oven and solder paste. * Second pass in developing your recipe comes through trail and error chan
Electronics Forum | Fri Nov 03 07:28:27 EST 2006 | davef
Via filling methods are: * Tenting * Plugging * Capping * Flooding Tented Via. A via covered with dry film soldermask; the via is not filled. When tenting from both sides there may be issues with trapped air that expands during mass soldering. Plug
Electronics Forum | Thu Nov 10 16:15:52 EST 2005 | 1st Article
Sumote, I suggest DESCO ESD safe het gloves, these gloves have a polyester exterior fabric with woven conductive fibers to ensure static protection. Inner lining constructed of material for use in heat assembly processes, can with stand 200�F maximum
Electronics Forum | Thu Nov 10 16:19:42 EST 2005 | 1st Article
Dear Sumote, I would suggest DESCO ESD safe heat gloves, we are using them at our facility, these gloves have a polyester exterior fabric with conductive fibers to ensure static protection. Inner lining constructed of material for use in heat of 200�
Electronics Forum | Tue May 30 21:09:30 EDT 2000 | Dave F
Dennis: Direct metalization is more of an European phenomena than a US one. Not to say that good things don�t come out of Europe. As background: Direct Metallization. In circuit board fabrication, an alternative to electroless plating makes the