Electronics Forum | Mon Aug 09 20:47:21 EDT 2004 | KEN
I think OA flux left on the pot would quickly looses its activity and become part of the dross waste stream, and smoke stream for that matter. Also, if your wave is setup properly your selective pallets will scour (push) the top of the lambda wav
Electronics Forum | Mon Nov 11 08:47:00 EST 2013 | mleber
Thanks guys. Here are more details. The cards are essentially the same. They use the same connectors, same footprint, the traces / layers would be comparable etc. The difference between the 2 we see is that one is laminate - Rigid Metal Clad Base, Ty
Electronics Forum | Fri Apr 14 11:00:38 EDT 2000 | Dave F
Mario: Your ask a very broad question and give no background information. Generally, the amount and type of residues present on a printed circuit board at the very beginning of a SMT line depends on the exposure of the board up to that point. For
Electronics Forum | Fri Apr 16 11:03:35 EDT 2004 | davef
Your copper corrosion is not good. It indicates that you have not done a good job in cleaning. [We assume this is a medium green color, not unlike the color of the solder mask on your board, that is almost like a translucent lacquer; rather than th
Electronics Forum | Mon Jul 10 21:01:06 EDT 2000 | Dave F
Edmund: Responding to your questions: 1 What is purpose of using DI water to wash a PCBA? Compared to tap water, DI water is less likely to leave: � Metal cations on sensitive components. � Salts of Ca, Mg, and other stuff on metals on the assemb
Electronics Forum | Mon May 15 11:03:13 EDT 2006 | Pitt Bull
Can lead free components/assemblies be contaminated if reflowed in a reflow oven for leaded process?
Electronics Forum | Thu Aug 16 13:06:59 EDT 2007 | shing
Will solder contamination related to PCB's surface finishing?
Electronics Forum | Thu May 18 10:42:41 EDT 2006 | stepheniii
I don't think so. But I want to point out the amount of lead needed to contaminate a joint is microscopic. You won't have lead vapour in your oven and with a clean oven there probably isn't any other way for even a microscopic amount of lead to con
Electronics Forum | Sun May 21 19:18:52 EDT 2006 | grantp
Hi, I think you should be ok, as the contamination in a reflow oven is generally flux from what I have seen. I have never heard to the solder metals itself being inside the oven apart from some paste in hole we did that sometimes dropped a bit of so
Electronics Forum | Wed May 28 11:56:18 EDT 2003 | blnorman
Yes we are using "silicones", but to find this contaminant we were looking for "silicon" the element by SEM/EDS. We use Dow materials and my contact there is checking to see if they have any info.