Electronics Forum | Tue Aug 14 23:58:19 EDT 2001 | Glen Brian
We are using the new auto-dipping machine for LED solder dipping and dragging. The flux is water-soluble flux and the solder is 63/37 at 250 deg. C. Two weeks ago we exchanged the pot with new 63/37 solder. About a week, we found that the high level
Electronics Forum | Tue Nov 14 22:01:07 EST 2000 | Dave F
I'd love to get to the point that I could discuss the impact of flux on dross formation. Until then, I fight with proper solder pot temperature, maintaining enough pump speed, and solder contaminants.
Electronics Forum | Fri Oct 05 11:14:14 EDT 2007 | Frank
Yeah, but when the operator drops regular solder bars into your lead-free pot, does that mean I should paint my bars, too?
Electronics Forum | Wed Aug 15 16:04:23 EDT 2001 | davef
First, responding to your question � Several things on copper dissolution in solder are: * A 50um copper wire will dissolve in 60Sn / 40Pb solder at: - 200�C solder in 55 seconds; - 250�C solder in 20 seconds; - 300�C solder in 5 seconds; - 350�C so
Electronics Forum | Wed Mar 10 13:53:13 EST 1999 | Vincent Vega
| We will wave solder a board with SOIC14 and SOIC16 parts on the bottom. It has been difficult to find any specific wave solder process recommendations from manufacturers of the SOICs. The pad geometry utilizes theiving pads on both sides to reduce
Electronics Forum | Tue Nov 21 22:15:59 EST 2000 | Vince Whipple
Mohammed, The first suggested place to start with your question would probably be with your flux Mfr. Push them! The quantity of dross is effected by several factors: The higher your solder pot temp., the higher your dross level... but don't go too
Electronics Forum | Wed May 26 10:00:03 EDT 1999 | David Scott
| | | | | | | | | | | | Any suggestions on how to maintain Adhesive dispensing nozzles??? They seem to plug up over night and it is starting to get on my nerves. We have tried leaving the nozzles in the machine, removing them and soaking in alcoh
Electronics Forum | Wed Jan 06 04:51:16 EST 1999 | Earl Moon
| | A question for you all! | | | | Back in the good old days, we didn't always know how clean was clean. Much has changed. Much hasn't. | | | | My question concerns cleaning under, through, and around tight spaces. Way back when, we could not clea
Electronics Forum | Tue Oct 12 17:40:01 EDT 1999 | Brian W.
| | | A question for you all! | | | | | | Back in the good old days, we didn't always know how clean was clean. Much has changed. Much hasn't. | | | | | | My question concerns cleaning under, through, and around tight spaces. Way back when, we coul
Electronics Forum | Tue Dec 08 12:44:52 EST 2020 | janwillemreusink
Who is using two sorts of tin in one selective soldering machine with to solder pots? So then the soldering program selects the correct pot (tin). What are the risks? Adding wrong tin in the wrong pot. Mixing up the nozzles?