Electronics Forum | Mon Mar 29 04:36:49 EST 1999 | Graham Naisbitt
Just for the record folks, The customer I believe may be manufacturing stuff for refuelling rigs of various forms. This being the case, the coating would need to be resistant against fuels and oils. The UR material (at least ours!) is able to resi
Electronics Forum | Mon Mar 29 19:17:47 EST 1999 | Scott McKee
How true, AR would not be the right choice... Scott | Just for the record folks, | | The customer I believe may be manufacturing stuff for refuelling rigs of various forms. | | This being the case, the coating would need to be resistant against f
Electronics Forum | Wed Jan 27 23:29:28 EST 1999 | parag palshikar
| | i am working with the noclean process and getting white residues on the bottomside of the board probably due to the | | wave soldering flux.i am using a no-clean solder paste and a noclean wave solder flux.The boards passed the accelerated tempe
Electronics Forum | Fri Mar 26 12:59:51 EST 1999 | Scott McKee
| | I am looking into replacing another business division's Acrylic coating process with our Urethane coating process. Unfortunately, MIL-I-46068 doesn't differentiate AR/UR's performance, and the MFR data sheets don't match up at all (they each spe
Electronics Forum | Wed Sep 30 18:43:46 EDT 1998 | Graham Naisbitt
Chrys, Please, refer firsatly to J-STD-001 Appendix D. Now, consider: SIR testing will help define the reliability of your finished assembly - it will not tell you how clean it is. Which do you or your customer prefer? Present SIR testing de
Electronics Forum | Tue May 26 19:20:39 EDT 1998 | Graham Naisbitt
Ryan, Please consider the following: There is no such thing as no residue flux. Low or no solids flux contain "wetting" agents to help the stuff stick upside down! Try painting your ceiling with less than 2% solids paint!! With all this excess liquid
Electronics Forum | Sun Apr 05 18:59:15 EDT 1998 | Graham Naisbitt
Jaqueline There are so many variables in the electronic assembly manufacturing process involving more than 12 different chemistries, that it is impossible to easily identify and determine the nature and reason of such residues. GEC Hirst Research in
Electronics Forum | Fri Jan 29 05:14:06 EST 1999 | Graham Naisbitt
Hi guys, I really am at a loss to understand this one. It would appear that there may be some reaction between the flux and the resist? Or maybe you have an OSP on the board that is reacting during soldering? As a fast fix, maybe you should try a
Electronics Forum | Thu Sep 17 11:09:32 EDT 1998 | Dave F
| I need an evaluation process to prove to a customer that our no-clean process does not leave excessive residue? Any ideas? Wayne: More of the same as Chry and Justin. KEY ISSUE The first thing that you need to know is: What does your customer me
Electronics Forum | Thu Sep 17 12:00:19 EDT 1998 | Mike C
| | I need an evaluation process to prove to a customer that our no-clean process does not leave excessive residue? Any ideas? | Wayne: More of the same as Chry and Justin. | KEY ISSUE | The first thing that you need to know is: What does your cus