Electronics Forum | Fri Feb 17 09:02:21 EST 2006 | russ
proper pad geometries, accurate placement, and good reflow profile. Are you having problems right now?
Electronics Forum | Thu Dec 14 21:53:07 EST 2006 | davef
Use the thermal recipe suggested by YOUR paste supplier, as the starting point.
Electronics Forum | Fri Jan 30 06:28:42 EST 2009 | gregoryyork
Hi Armando Hotflow 7 is a big machine and one of the best Reflow ovens around (in my opinion), well suited for Lead Free. A typical 1.6mm board has the following settings for Lead Free SAC305 paste All Temperature settings are Top and Bottom Prehea
Electronics Forum | Sat May 28 06:43:03 EDT 2005 | steve
I have the ability to offer both SAC and SN100C lead free alloys to my customer base. What might occur if a customer is already using SAC305 in their wave and they want to save money and go to SN100C. They now are mixing, tin,silver,copper with tin,c
Electronics Forum | Wed Nov 02 11:14:45 EST 2005 | Doug
I am doing lead free testing on a Vitronics selective machine with a 4 mm nozzle. The finishes I am testing are ENIG, ImSn, and ImAg. The problem I am encountering is achieving good top side wetting. Has anyone had any luck with this type of an ap
Electronics Forum | Fri Feb 17 11:01:47 EST 2006 | amol_kane
with lead-free solders, one would expect to find less instances of tombstoning. this is because SAC alloys are not eutectic and melt over a range of temp (usually 217-220 deg C) instead of at a single temperature. therefore the forces due to solder s
Electronics Forum | Tue Dec 12 01:52:05 EST 2006 | hemu_me
As we have vitronics oven(SMR610A) made in dec,1997,which has 5 heating zones and 2 cooling zones. For Lead free soldering what should be our baseline for low/medium boards.we have gathered profiles from various paste manufacturers,however we don't k
Electronics Forum | Thu Jan 29 06:29:33 EST 2009 | sachu_70
There are two profiles available for the Pb-free process: (1) RSS and (2) RTS. In your case, you should try a solder paste that supports RTS profiles. A minimum of 7 zone Refow Oven would be fine on the Pb-free process. However, you may still try by
Electronics Forum | Thu Jul 26 23:57:47 EDT 2007 | gioblast
Good day.. anyone who have read the best guide on pb-free pcb plating?? I know immersion is the best but the storage controls sucks..easily changes color..ANYONE WITH A BETTER kNOWLEDGE ON HOW TO CONTROL? OR better plating ...enig?? why?? please. all
Electronics Forum | Wed Nov 17 07:39:20 EST 2010 | jax
Most PCB manufacturers should be able to fall between 1.25um-5.00um for Pb-Free HASL. I doubt you will get anyone to agree to anything higher. If you are going to require an average thickness, make sure you also state "No Copper exposure allowed".