Electronics Forum | Tue Jun 01 08:53:16 EDT 1999 | James Whitehouse
We have experienced problems with chlorine damaging certain components, is there anyone with similar problems and possible solutions ? preferably info about a source for chlorine free solder paste Thanks James
Electronics Forum | Tue Oct 18 19:34:02 EDT 2011 | warwolf
so there is no one here baised in New Zealand that wants to buy our SAC305 solder dross and recycle it, we have about 120KG at the moment, anyone intrested?
Electronics Forum | Fri Oct 28 21:46:35 EDT 2011 | rdh_41
Hi , I'm interested in Tin and hoping to open long-term business relationship with your company. We are Taiwan-based company dedicate in Tin (Sn). We are looking for opportunity to work with you. And it would be great if you have large quantity of t
Electronics Forum | Wed Feb 21 14:14:11 EST 2007 | rgduval
Hi, Bill, Lead-free solder and paste manufacturers will be a great resource for you during the transition; they've tested their products extensively, and their application groups have been able to help me through the biggest changes. There are a fe
Electronics Forum | Wed Jan 07 15:48:22 EST 2015 | jacklucas
We switched our PCB's to 170Tg over 10 years ago, so we're probably good to go on the temperature aspect. Thanks for the opinion on the added lead content.
Electronics Forum | Wed Jan 07 14:33:00 EST 2015 | eezday
The assumption that a HASL Sn63 PCB can be soldered with SAC solder paste is likely a bad one. The board itself is likely FR4 which can be damaged by lead free temperatures. The HASL finish isn't an issue from the perspective of it's makeup and actu
Electronics Forum | Mon Jul 16 10:51:09 EDT 2007 | patrickbruneel
D. Hillman, et al., �The Impact of Reflowing a Pb free Solder Alloy Using a Tin/Lead Solder Alloy Reflow Profile on Solder Joint Integrity,� International Conference on Lead-free Soldering, CMAP, Toronto, Ontario, Canada, May 24-26, 2005, http://www.
Electronics Forum | Wed Nov 23 00:22:30 EST 2005 | mskler
Thanx for your only reply!! I already increased temprature now its actualy on board is 240*c. I would like to discuss one more thing if I go for lead free solder paste & using some components wich are not lead free then what will be the result. Has a
Electronics Forum | Tue Jan 06 16:31:41 EST 2015 | jacklucas
In switching to lead free processing, we find ourselves having over 400 PCB part numbers with Sn63 HASL finish. And there is no hope of quickly purging inventory and getting our drawings changed to call out a lead free finish. I want to avoid having
Electronics Forum | Thu Jul 19 04:38:33 EDT 2007 | chrispy1963
I took a Lead Free troubleshooting Class at SMTA in Chicago last September taught by Phil Zarrow. He told us during that seminar that its not a good practice to cross contaminate Leaded and Lead Free components but IF it is necesary than using lead