Electronics Forum | Mon Dec 22 16:09:02 EST 1997 | Justin Medernach
| I am designing an SMT pad for a ss metal switch. | Finished copper thickness is .0014 and nickle-plating | originally is 150 millionths. Initial testing yields 100,000 to 150,000 switches before intermitent failures (copper is reached.) I want 50
Electronics Forum | Fri Oct 08 17:12:31 EDT 1999 | Dave F
| Hi, | | Does anybody know what is the minimum gold plating thickness on the PCB goldfinger required by the industrial specifications - IPC, Bellcore, etc. Where can I find the information? Appreciate for the help! | | Thanks, | Tony | Hi Tony:
Electronics Forum | Thu Nov 10 12:29:57 EST 2022 | stephendo
The G in ENIG is gold. It does not oxidise. Either you are thinking of OSP or your board shop is providing defective boards if your boards show oxidation. It would be the nickel that is oxidising but should be totally covered by the gold. Is there
Electronics Forum | Thu Nov 10 20:39:44 EST 2022 | SMTA-64386598
The solderability shelf life of ENIG is related almost entirely to diffusion of O2 through the gold plating. When O2 diffuses through the gold, the underlying nickel is oxidized rendering it unsolderable (with ENIG - you solder to Ni, the gold dissol
Electronics Forum | Fri Jan 06 00:03:10 EST 2023 | SMTA-64419298
Hello Evtimov, sorry...just saw post as I was looking through list...a bit late. I don't know if you ever got your answer. IPC-4552A covers EniG finishes and suggested shelf life. I've referred to these doc's quite a bit. Good spec's ! Yes, I beli
Electronics Forum | Mon Mar 30 04:33:48 EDT 2009 | 89jeong
Hi all We also met the solder nonwetting problem as below. This happend after reflow and this is Rohs cpmpliant. How do i solve this problem? Thanks
Electronics Forum | Tue Mar 31 05:26:14 EDT 2009 | d0min0
Hello, we had similar problem in the past - when we had to change PCB supplier from a batch of hundreds of boards (NiAu plated, SnPb process) we got 2-3 boards with paste wicking to components leads what we did, was to check the thickness of gold on
Electronics Forum | Tue Feb 03 16:42:50 EST 2009 | cuperpeter
Hello All, > > I have a problem with nonwetting Au > finish after second cycle of reflow soldering > doublesided boards. Solder nonwetted pcb pads (is > wicked to component terminations) Either these > pads or some of non component pads became
Electronics Forum | Sun Jan 25 17:40:16 EST 2009 | cuperpeter
Hello All, I have a problem with nonwetting Au finish after second cycle of reflow soldering doublesided boards. Solder nonwetted pcb pads (is wicked to component terminations) Either these pads or some of non component pads became discoloured from
Electronics Forum | Mon Jan 26 11:14:08 EST 2009 | evtimov
This one might help http://www.smtnet.com/Forums/index.cfm?fuseaction=view_thread&CFApp=1&Thread_ID=13630&mc=5 Emil