Electronics Forum | Sat Aug 29 08:43:35 EDT 1998 | Dave F
| Hi, Friends, | Could you please recommend me some solder mask materials and equitements for high quality solder mask? Details such as company name, phone numer et al are welcomed. Thanks! | Have a good day | Xingsheng Xingsheng: Consider the follo
Electronics Forum | Mon Nov 27 19:32:02 EST 2000 | Michael Parker
Prof. Whoopee - amazing facts that you find on your 3-D BB, it has completely confounded my comrade, Chumley. Plainly spoken that around the SF Bay Area a.k.a. Silicon Valley(ever hear of the famous SF Fog?)during the winter months, near the coast a
Electronics Forum | Fri Mar 24 11:12:06 EST 2006 | patrickbruneel
You�re a good man Rob and a good patriot, you defend your governments decisions even if they're wrong. Isn't the WEEE directive aimed at preventing electronics ending up in a landfill? This immediately takes away the leaching arguments and is a great
Electronics Forum | Mon Nov 09 09:44:22 EST 2015 | davef
Purpose. This describes setting-up a wave soldering system set-up for a new assembly design or checking a wave solder machine operation with a test board. Applicability. To be used for new design printed circuit assembles and during machine accept
Electronics Forum | Tue Apr 09 21:40:26 EDT 2002 | ianchan
We are a local enterprise with limited resources, just like you described, so hope this experience sharing helps : we place a production Visual Mechanical Inspection (VMI) inspector at the end of each Reflow Oven area, complete with magnify scope 30
Electronics Forum | Wed Apr 30 12:26:10 EDT 2008 | dphilbrick
There must be discussions about this on SMTnet but I have yet to find them. I would like to hear from all you smart people about running LF and PB BGA�s on the same board using 63/37 solder. If you run your profile up to peak at around 225C +/- (nitr
Electronics Forum | Tue Oct 05 12:46:02 EDT 2021 | emeto
From what I understand SAC305 and SAC405 are considered low silver content and have the better overall mechanical qualities compared to more silver or no silver.
Electronics Forum | Thu Jul 15 09:34:24 EDT 1999 | John Sims
I'm looking into vision inspection equipment to automatically inspect SMD placement and solder joint quality. Does anyone have any recommendations or know of any commonly used equipment? Do other manufacturers use vision systems at their inspection
Electronics Forum | Fri Mar 26 15:48:31 EDT 2021 | grahamcooper22
Leaded HASL on small pads can be quite difficult to print on...the HASL tends to be domed rather than flat..and that can affect print quality...you really need a perfectly flat pcb pad to print paste on when you are assembling 0.5mm QFPs. If the pcb
Electronics Forum | Fri Mar 09 05:06:09 EST 2012 | grahamcooper22
Is your solder paste deposit drying out? Or if the paste deposit is small or there is insufficient paste then the tack between the device and paste will be poor so it can easily come out of the paste during its placement or placement of other parts.