Electronics Forum | Fri Oct 19 10:49:48 EDT 2007 | brulal1
Hi I will like to know what do you think about cleaning hand solder, my employee spend about 25% of they time to brush they hand solder with teddy pen cleaner, we used no clean solder wire. It�s not been the first time that I try to eliminate those c
Electronics Forum | Wed Dec 08 05:41:49 EST 2004 | kanwal324
Hello I thind you are same Mr. Scott from whom once i had purchased inspection system in M/s Evershine India. Regarding your query, we want to inform you that we are mounting BGA with water solubel flux (special flux paste) from alpha metals and the
Electronics Forum | Tue Dec 07 17:40:30 EST 2004 | davef
We'd suggest listening to your CSP component supplier. The standoff is too low. Check with your flux suppliers for the information you seek.
Electronics Forum | Mon Dec 13 16:25:37 EST 2004 | saragorcos
Hi Scott - No clean assemblies have a very low tolerance for processing residues, and long term reliability is compromised if residues from incoming bare boards, components, or un-solublized flux residues are not dealt with. It is critical to contro
Electronics Forum | Sun Sep 27 23:10:19 EDT 2009 | hallwayit
Hi, Walter, Why don't you try no-clean flux? We ever met the same condition, later, we changed to no-clean flux solved the problem.
Electronics Forum | Wed Jan 17 10:01:49 EST 2007 | lyetc
Hi...have you try ultrasonic cleaning before rinsing?
Electronics Forum | Wed Dec 27 20:33:50 EST 2006 | greg york
water alone especially cold is not good enough, how do you check for hasl fluids when most residues left behind after improper cleaning are non ionic. Use 40C saponifier followed by heated rinse then cold rinse then DI rinse followed by dry.Nylon bru
Electronics Forum | Mon Jan 15 11:43:13 EST 2007 | fredericksr
celsius or fahrenheit? I am not entirely familiar with the deeper details of HASL, but 130F-140F is adequate to clean many of the water-soluble fluxes used for component soldering.
Electronics Forum | Thu Sep 03 11:20:41 EDT 2009 | thunderdog5000
I have a customer that is having a flux residue problem after wave soldering. Flux is roaring through the board to the top side and leaving a residue. This is only happening on the flat stamped leads. The round leads are fine. They are using Supe
Electronics Forum | Fri Jun 19 18:44:23 EDT 1998 | Steve
Does anyone have wave solder experience using OSP and VOC free no clean flux?