Electronics Forum | Fri Oct 14 11:56:49 EDT 2005 | patrickbruneel
Mika, 1.) Is there a maximum board thickness where it would be almost impossible to get a decent hole fil? Answer: The thicker the board the further the solder has to travel and the more you depend on solderability of boards and components, machine
Electronics Forum | Thu Apr 20 14:59:11 EDT 2017 | davef
It's difficult to tell anything from your picture. But playing the odds, I'd say it's not "gold corrosion." It is very difficult to corrode gold. Gold is a NOBLE metal. From Wikipedia, the free encyclopedia In chemistry, the noble metals are metals
Electronics Forum | Tue Jan 05 19:25:50 EST 1999 | Earl Moon
| Jan 05, 1999 | | My question is: | Pls kindly advise what is the meant by a "Think Film hybrid design" and what are the advantages it would have on surface mount passive components e.g. capacitors and reisitors?? | | Thanks for your respond. | El
Electronics Forum | Fri Feb 01 08:35:18 EST 2002 | gregers
PWB shelf life: HASL---3mth ENTEK-- 2mth Before using expired PWB, it is suggested to go thru HASL or ENTEK angain. Ask your VDR to serve this. Re immersion Au, mostly when the thickness under 3u"(micro pores present), the surface gold will serve a
Electronics Forum | Wed Feb 21 21:01:57 EST 2007 | davef
Yes. Heat reduces OSP solderability protection thickness. For instance, many OSP are shot at the end of the first reflow pass and the exposed copper is free to oxidize. If you're speedy, you can pull-off the second reflow cycle before the copper g
Electronics Forum | Fri Apr 09 20:47:36 EDT 2010 | 89jeong
I think the oxidation on the pad happens easily but do not on Au plated pad.The reason may be caused by improper cleaning or Au plating thickness in plating process. But,before suspecting the pcb board, you need to check your process or used material
Electronics Forum | Wed Nov 06 03:51:28 EST 2013 | cuperpeter
Hi rob, Thank you very much for your response. Profiling was made exactly on the pad, which showed dewetting, so the values are mentioned for this pad. PCB's is about a week old. It is possible that the surface of pads is already oxidized? I will t
Electronics Forum | Sat Nov 14 08:58:38 EST 1998 | Earl Moon
| I keep hearing about polyimide stencils, but what are they like in terms of registration and aperture accuracy? | You are hearing about polyimide as in polyimide film as Kapton (TM Dupont). This material is the stuff of flex and rigid/flex circuit
Electronics Forum | Tue Jun 28 18:20:49 EDT 2005 | russ
Matt, have you run a profile on this board? Just because it's .062" doesn't mean that any old .062" profile will work. We have .062" thick boards that almost nil for copper and other are utilizing 2 oz. layers internally. They require quite diffe
Electronics Forum | Mon Aug 10 11:28:19 EDT 1998 | Justin Medernach
| Is there any problem using SMT on gold boards? 15 years ago we were told not to use gold boards, but I can't remember why. Judging by the other postings it now appears to be common. Only problem I see is that the nickel should be plated, not ele