Electronics Forum | Tue Dec 08 12:44:52 EST 2020 | janwillemreusink
Who is using two sorts of tin in one selective soldering machine with to solder pots? So then the soldering program selects the correct pot (tin). What are the risks? Adding wrong tin in the wrong pot. Mixing up the nozzles?
Electronics Forum | Tue Jul 08 12:21:42 EDT 2008 | jwasyliw
Biggest differnce is tooling. Tooling cost with > a fixed pot - no tooling cost with programable > "moving"pot. > > There are various way to control > peel off with a moving pot. Depending on the > machine, you can use either the Z axis or the
Electronics Forum | Thu Jan 12 17:42:55 EST 2012 | warwolf
yeah we are getting quotes on a new solder pot, we have used that paint we tested a small sample of it with solder and it seems to be ok, we are doing a full solder alloy change in about two months so we will have a chance to inspect the solder pot a
Electronics Forum | Sat Oct 08 04:24:37 EDT 2016 | aaronpainter
We are having an issue with the solder bars hanging the solder feeder dripping down the back side of the pot, and leaking in to the area where the terminal block for the elements on the pot are. We have tried aluminum tape to close off the gap betwee
Electronics Forum | Mon Jun 12 07:52:21 EDT 2017 | tch
We have had this issue on our Delta 3 waves and determined that there are small pin holes in the solder pot. We had plates welded to the outside of our solder pot on the lead free wave and this bought us enough time until we could replace the wave, a
Electronics Forum | Thu Dec 10 05:58:59 EST 2009 | gregoryyork
Best to use Tin treated with TinP Additive. This ensures the Tin is fluid enough to Dissolve any Leaded residues. Run the machine for one hour at 275C then take out wave former and as much of the workings of the pot as possible. Then start bailing ou
Electronics Forum | Mon Apr 22 09:07:43 EDT 2002 | pjc
Francis, The potting encapsulation process was in the mfg. of flash-disk devices built on a DIP formfactor. Compact flash do not normally get potted. Ultrasonic welding or snap-togther is methods for closing the compact flash housing. The potting mat
Electronics Forum | Mon Jun 23 11:24:12 EDT 2003 | procon
Titanium components are best for any suface in contact with lead free solder. We will be offering our brand solder fountain rework station utilizing Titanium components in July. Lead-Free solders seem to adhere to SST or cast pots and cause blockages
Electronics Forum | Fri Feb 25 18:13:17 EST 2005 | davef
Your leadfree dross should float, similar to your leaded dross. It's possible you're thinking about the process for removing excess copper from the solder pot. Following the same process, with: * Leaded solder, the copper floats. So, you scoop the
Electronics Forum | Tue Oct 04 18:45:44 EDT 2005 | MikeF
How do you drain out the solder at the bottom ? I thought most solder pots have a channel from the pump impeller to the bottom of the nozzle. When you get down to that point is that when you use the drain? I've managed to not have to drain a big po