Electronics Forum | Mon Nov 10 13:14:34 EST 2008 | evtimov
Hello Hoss, try with the flux again. I would first change the flux. Alcohol based for me is always better. But you can try water based too. 1. Change the flux 2. Go with more pressure on your atomizer(or whatever they call it on your machine). Just
Electronics Forum | Thu Oct 28 08:28:33 EDT 2010 | d0min0
Hi, previous topics found closed so I couldn't continue on them, but wanted to ask maybe something that we don't already know paste shape and placement ok, reflow 12 zones profile looks ok (same since 2 yrs), component placement ok, one reference i
Electronics Forum | Fri Jun 09 09:57:17 EDT 2023 | tommy_magyar
Regardless of what you choose, pay particular attention on the support they offer. Location of manufacturer/distributor office to be in a couple hours of driving distance, so if there is a problem, they can reach you quickly. We use Inertec - no maj
Electronics Forum | Wed Aug 26 16:19:48 EDT 2020 | kylehunter
Great! Thanks a lot for the help Definitely nice when everyone is in complete agreeance. I do think going to liquid nitrogen, then a generator makes sense. Currently we aren't planning on using the machine daily, so we'll probably hold off until we a
Electronics Forum | Fri Nov 20 00:16:24 EST 2015 | bwetman
Hyperterminal is a standard Windows assessory located in the "Communications" folder.Here are some steps of data received through the hyperterminal in the PC. (1)Connect your device with your system through RS-232 cable or USB-to-Serial adapter and c
Electronics Forum | Tue Oct 05 02:24:58 EDT 2004 | darby
What config are you replacing? ie 1 machine, 2 x 3machine lines, 1 x 2 machine line etc. What do you want to place with it? I can't comment on the Contact machines having never used one. On Samsungs I will say this. For your own benefit consider the
Electronics Forum | Wed Nov 12 18:58:19 EST 2008 | joeherz
I attended SMTA's copper dissolution webinar this morning and am almost convinced that this is not our problem. Still planning to do cross sections to verify but our dwell times are nowhere near levels that could cause a problem assuming good platin
Electronics Forum | Sat May 29 02:20:08 EDT 2010 | vinitverma
Mch Adjust > Adjust Target > Laser Unit > Nozzle Position. Here the laser will automatically detect the centre of the nozzle. Remember - It'll give you the option of using a component for the test but DON'T use any component. Let it detect the centre
Electronics Forum | Tue Oct 11 09:26:42 EDT 2011 | dilogic
For all of you that are using this version of GSM USOS, I've made a patch that changes default fiducial repair drop-down menu from "Reteach Fiducial" to "Alignment Done". We had a large batch of boards with lousy fiducials and it drove me crazy havin
Electronics Forum | Thu Jul 12 21:41:35 EDT 2001 | mugen
A) Questions: 1) What sort of pallet materials used? 2) what PCB thickness & LxW size? 3) what stencil type & thickness used? 4) what profile type used (peak deg-C)? 5) any peak Deg-C contraints for the components SMT onto the PCB? B) We use pallet