Electronics Forum | Fri Jun 09 10:01:39 EDT 2017 | jkitt84
Ed, this is great info. Thanks. Jeff
Electronics Forum | Thu Jun 08 09:43:42 EDT 2017 | davef
You know the scary part about your mentioning a tread where I post something? Well. let's just say that 2007 was a long time ago. Anyhow, silver will dissolve into your solder and provide no barrier. Some people apply a silver flash plating over the
Electronics Forum | Thu Jun 08 18:19:40 EDT 2017 | edhare
Jeff, You might look at this paper, which has some background & references that are relevant to your question ... http://www.semlab.com/papers/diffusionbarrierplatinginelectronics.pdf Ed Hare
Electronics Forum | Thu Jun 08 11:37:44 EDT 2017 | jkitt84
davef, thanks for feedback. I talked with a plater who said they put copper before silver when plating brass. Would a complete stack of: Brass part, then 0.0001-0.0002" of copper, then 0.0005" of silver, then Tarniban anti oxidation. Sound reasonabl
Electronics Forum | Thu Jun 08 07:56:34 EDT 2017 | jkitt84
In an excellent previous thread davef mentions brass should be plated prior to soldering to prevent zinc leaching from the brass. It is reported once the zinc leaches, the joint is weak. He recommends copper or nickel plating. Would silver plating w
Electronics Forum | Thu Jun 08 16:12:19 EDT 2017 | davef
Your plater's recommendation should work fine. Your simple copper plate will work, but you'll be stepping into fighting a copper tarnish battle. Silver over the copper is a better choice. I was thinking a silver thickness of a minimum of 3 microns
Electronics Forum | Fri Nov 19 01:55:44 EST 2004 | Chics
Hi, Is anyone aware of the Mesh sizes(Screen Printing) that are against specific silver particle sizes. Like in case of solder for different types of paste, different mash sizes are recommended. Is anyone aware of any such things in the case of silve
Electronics Forum | Mon Apr 01 07:41:40 EST 2002 | davef
Hey Bob, Boy, you are lucky to have a laboratory, and now colorful pix!!! The only silver IMC that you will see are: * Ag6Sn, much less likely at 'normal' soldering temperatures * Ag3Sn, much more likely Allowable silver concentration: * Below 2%
Electronics Forum | Fri Dec 15 08:00:57 EST 2000 | Pete B
John, We regularly wave solder electroless silver finished boards (Alpha Level)with mixed SMD and through hole parts and do not have any problems. We have changed a number on PCB's from HASL to electroless silver, mainly for the benefits at SMD whe
Electronics Forum | Sun Mar 31 10:03:25 EST 2002 | Bob
Cheers Dave, to answer some of your questions. � The component lead is copper with a tin / lead coating. The pads are standard Copper / Nickel / Gold. � The solder is standard Tin / Lead / Silver (2%) We have a lab that can determine the composition