Electronics Forum | Sat Jan 03 17:43:31 EST 2009 | proy
Hi Wondering if anyone here is/are filemaker Pro users? I am writing a simple data collection program in Filemaker for pre-solder, pre-test inspection to replace paper sheets. Together with wireless touchscreen tablets I think this is going to be
Electronics Forum | Tue Feb 29 21:53:46 EST 2000 | Kelvin Chow
Dear Robert, On PBGA assembly, BGA sphere shrinkage number depends to the following factors, a. BGA Sphere size (before reflow) b. Solder mask opening diameter As far as I know, no formular has been established yet. Most of my friends just collect
Electronics Forum | Tue Feb 29 21:53:46 EST 2000 | Kelvin Chow
Dear Robert, On PBGA assembly, BGA sphere shrinkage number depends to the following factors, a. BGA Sphere size (before reflow) b. Solder mask opening diameter As far as I know, no formular has been established yet. Most of my friends just collect
Electronics Forum | Fri Apr 06 04:10:25 EDT 2001 | kensmoke
We recently had a multi block panal change at the vendor Now the production lines are producing solderability defects in great number. The makeup of the pcb is a type of fiber glass mask green in color and pads with no tinning just copper lands.
Electronics Forum | Thu Dec 05 11:36:30 EST 2002 | William Guatemala
Have you check the flux gravity lately? If not, Check the flux gravity every 6 hours to make sure proper parameters are meet. Here is a list of things that may cause your solder ball problems; Excecive heat, defective fixtures, preheating temperature
Electronics Forum | Mon Dec 16 19:05:57 EST 2002 | davidduke
Steve , I agree with all the responses you have received. Randy Villeneuve is absolutly correct in all of his assesments and I would consider him an expert with the process , Gris is correct about adding a "heat sink" to the process complicating pr
Electronics Forum | Wed Feb 16 14:47:04 EST 2005 | Valerie
Mike, To answer your question, Yes we have thru-hole parts on the boards that we converted to double-sided reflow, we use pallets to select solder the leads. I suppose Masking would work, but that's using a lot of mask. Can I ask, whats preventing
Electronics Forum | Mon Dec 18 14:36:09 EST 2006 | samir
Yikes!! In-line cleaning, to clean cosmetic and benign residues (from a NO-CLEAN) flux... You sure you can't switch fluxes? Another variable with residues is the solder mask. Depending on mask type (glossy, matte, semi-gloss, or semi-matte), will
Electronics Forum | Wed Dec 20 04:43:36 EST 2006 | greg york
Any decent flux would volatise off with the heat of the wave unless absorbed into the solder mask. Test this by trying to clean in alcohol or common solvent aerosol, if it does not clean then it is probably Mineral Salts from solder mask fillers. Ano
Electronics Forum | Wed Feb 09 21:19:03 EST 2005 | Mrduckmann2000
Russ, We can not use a wave pallet, already went that route. We have parts next to the thru-hole pins and between thru-hole pins. I am going to try an experiment in the next day or so with solder mask. I plan to solder SMT parts on the back of se
Our Company handle AOI (Auto Optical Inspection) and SPI (Solder Paste Inspection) Machines.
Equipment Dealer / Broker / Auctions
Hwaseong-si, Gyeonggi-do, Korea
Hwaseong-si, South Korea
Phone: +82-1029254936