Electronics Forum | Mon Oct 12 20:51:14 EDT 1998 | Eric
| | Came a cross an interseting observation/question. | | I'll need to filter additional information and specifics to those whom may be able to assist me. But for now; | | | | I use a water soluble base organic flux manufactured by Kester (the exac
Electronics Forum | Mon Mar 29 09:33:37 EST 1999 | Chrys Shea
| I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | What disadvantages are there when using this flux? | Do you have any contact details with
Electronics Forum | Tue Mar 30 08:11:27 EST 1999 | George Steele
| | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | What disadvantages are there when using this flux? | | Do you have any contact detail
Electronics Forum | Wed Apr 28 12:08:02 EDT 2010 | tjg
Our latest designs are flip chip on flex based and we have issues with delamination/blistering. We know it is related to our vapor solvent (n-Propyl Bromide based) attacking an inner layer adhesive. Has anyone else ever heard of something like this?
Electronics Forum | Mon Apr 05 08:25:31 EDT 1999 | ADRIANO FERNANDES
| | | I require some feed back from any one who knows about using a voc free flux in a nitrogen wave solder machine soldering both through hle and smt componants. | | | What disadvantages are there when using this flux? | | | Do you have any contact
Electronics Forum | Thu Apr 01 21:18:31 EST 1999 | Chris Kelly
Glenn, There are both very good VOC-Free fluxes as well as alcohol based fluxes out there. This should be your primary focus if you are so lucky as to have to opportunity to actually select a flux! The use of nitrogen will benefit any no-clean pro
Electronics Forum | Tue Jun 19 12:26:38 EDT 2007 | billr73
We will be hand soldering a small number of PCBs per week (both through hole and SMT) using a water soluble flux. We will be using both standard leaded and lead free solder. The completed assemblies be hand washed in a sink using hot water. Do we
Electronics Forum | Tue Jun 09 18:44:20 EDT 2009 | dyoungquist
We are using a water soluble flux which requires the assemblies to be cleaned in an ultra sonic cleaner after assembly. Is there a standard that specifies how long the assemblies need to be baked/dried after being submersed in a water solution for a
Electronics Forum | Thu Sep 06 10:58:54 EDT 2001 | Steve
If I had to deal with this problem, I would switch to water soluble paste. It is a much more cost effective solution.
Electronics Forum | Mon Sep 20 12:19:13 EDT 1999 | Brian
| Hi all, | | We have a little discussion here about the suitable flux for a certain process, as all of us are beginners we need your advice. | | We are producing VGA cards and mother boards for PC's all components to be wave soldered are TH, the S