Electronics Forum | Thu Mar 20 09:01:33 EDT 2008 | meritajs
Thanks Greg Our main problem is that we are putting small number PCB through, about300 PCB, size180*250. Such number order our customer in week. In result we got such high solder consumption and high production cost. We will tray to use antiacidant.
Electronics Forum | Fri Mar 21 08:39:38 EDT 2008 | lococost
If you are saying you're going through 1kg/h while only producing 300 pcbs a week and the rest of the time the machine is standing still, then 1.there is something seriously wrong with your machine or 2. check if an operator is suddenly covered in sh
Electronics Forum | Wed Aug 10 10:41:23 EDT 2005 | patrickbruneel
Bob, Great theory if you're selling SN100C, but I have to disagree that an alloy being 4�C off eutectic will cause cracks. When a solder joint exits the solder wave, there is an immediate drop in temperature of 100�C. so being off 4�C is irrelevant.
Electronics Forum | Wed Aug 10 09:01:15 EDT 2005 | fctassembly
Hello Joseph, Sorry for the bad news but microcracking is a well known potential condition occuring with the SAC305 alloy. Microcracking is a condition being seen with many joints soldered with the SAC305 alloy. It is technically a shrinkage cavity
Electronics Forum | Thu Dec 01 05:23:55 EST 2016 | stivais
Rob Just wondering - have you made analysis of your solder alloy on a regular basis? We are using SAC305 but stainless steel parts (e.g. a nut or a washer) dissolve quite quickly.
Electronics Forum | Sun Nov 27 05:04:02 EST 2016 | pmcg
Never used stainless pots as when we converted to lead free we changed all the pots to titanium. Been using SN100C for many years now, very good results, also use it in reel form in our selective solder machines with great results. Bear in mind the
Electronics Forum | Wed Oct 12 11:19:46 EDT 2005 | patrickbruneel
Yeah, adopting is the right word. In this new lead-free era spec.'s are made to stay within the scoop of the RoHS directive. The driving force for spec.'s should be reliability. Did you see any impurity level spec.'s yet in wave soldering for Cu, Au,
Electronics Forum | Tue Apr 29 07:12:49 EDT 2003 | Glen barden
Sn/Cu/Ni is introducted to me in wavesoldering lead free process. Around in our industry, we have a plenty of info. about SAC but not on this alloy. The distributor showed me some information about this alloy including less dross, more shiny /smoot
Electronics Forum | Thu Mar 11 01:54:55 EST 1999 | Marcus Reichenberger
Hello everyone, at the Institute for Manufacturing Automation and Production Systems of the University of Erlangen (Germany) one focus of our research activities is the use of lead-free solder alloys for electronics production. In different publicat
Electronics Forum | Wed Oct 10 02:04:10 EDT 2007 | omidjuve
hi we use a no clean solder paste with the sn63pb37 alloy and our high frquency board doesn`t have any problem in test but after this product is finished now we use 2 different solder pastes 1. sn62 pb36 Ag.4 RA tape 2. NC type lead free with Ag i