Electronics Forum | Tue Feb 19 08:41:02 EST 2019 | prasanth
dear experts, i want your suggestion for getting a profile in Heller 1707 mk iii series re-flow machine ,its 7 zone machine recently we had a solder ability issues , so pls guide me ,how to set rts profile parameters
Electronics Forum | Mon Jun 07 17:28:07 EDT 2004 | edatasys
LSP is 'Long Soak Profile'. See http://www.aimsolder.com/tds/NC_297DX_Sn62_&_Sn63_Solder_Paste.pdf Looks like a variation of the RSS, with you guessed it a longer soak.
Electronics Forum | Wed Sep 26 14:48:01 EDT 2001 | bobm
there is a company called EFD. my contact there is john kaminski. they have thermocouples that are spring loaded requiring no solder at all. they work great. you attach them to the edge of the board and you can move the end to make contact where you
Electronics Forum | Sat Sep 22 09:07:56 EDT 2001 | davef
Back-stepping a bit. If a profile is being used to: * Set-up the oven for a new product or trouble-shooting process, the profile should be taken with a solid contact to a solder connection. * Monitoring on-going stable and in-control process that re
Electronics Forum | Sat Sep 22 14:33:50 EDT 2001 | Tony
I like to secure the thermalcouples with a small dot of chip-bonder(surface mount adhesive). The chip-bonder will cure durring the first pass through the oven. After I have developed my profile I remove thermalcouples and the chip-bonder with a solde
Electronics Forum | Fri Sep 21 09:29:49 EDT 2001 | steven
when taking a reflow profile, can i attach the thermalcouple to the component body (using high temp tape) instead of to the leads (often found thermal couple dettached during reflow). in general, what is the temp diff between these 2 locatinos. if so
Electronics Forum | Mon Jun 07 21:26:03 EDT 2004 | davef
First, voiding is a process indicator. Next, as you say, the profile is a significant contributor to void formation. Finally, when considering the "material factors" that drive void formation, solder paste formulation is the most critical. Discuss
Electronics Forum | Sun Sep 09 16:03:50 EDT 2007 | davef
Wave Optimizer-person Help us understand how your "excellent wave solder guide called 'Take No Prisoners' that includes instructions for attacking and eliminating solder balls and preventing their recurrence" will help Joris resolve his / her issues
Electronics Forum | Thu Feb 26 16:49:57 EST 1998 | specnor tecnic corp
we have some rebuilt wave soldering systems in stock ready to be shipped. epk-ii smt with lambda wave, chip wave ,omega wave. 4 preheaters,jacking stand roll out computer control. machine is in a great shape. another machin upk15f with 6 preheaters
Electronics Forum | Tue Sep 12 04:48:26 EDT 2000 | Daniel
Is there a risk of popcorning plastic components during wave soldering? (The PCB is first surface mounted, reflowed and washed. It is sometimes left in air environment for as long as 48 h before the throgh hole components are mounted and they are wa