Electronics Forum | Tue Dec 10 14:10:38 EST 2002 | Randy Villeneuve
Steve, I wave solder most if not all our boards with selective wave pallets. I did not catch if the solder balls were on top of the board or on the bottom but that will make a difference on what to do to get rid of them. Pallets are good and bad. On
Electronics Forum | Thu Dec 05 11:04:27 EST 2002 | slthomas
They're IR, bottom side only. Frankly wave solder is not my forte (there are those that would claim nothing is), but I've personally been tasked with developing a process to do reliable, high volume bottom side SMT, so I'm drawing a lot from the tec
Electronics Forum | Fri Dec 06 18:13:15 EST 2002 | slthomas
We only have solder balling problems in the interface of the pcb with the selective soldering pallet. All other boards (single, and double sided glue and waved alike) are fine, so I'm not thinking this is going to follow the normal path for resoluti
Electronics Forum | Tue Dec 17 08:38:30 EST 2002 | Randy Villeneuve
Jim, In most cases if you can eliminate a process you will save money. With that in mind, an all surface mount or all through hole design is prefered. There are alternatives to that rule, like hybrid designs that can be pin and paste soldered. It al
Electronics Forum | Thu Jan 27 11:23:45 EST 2005 | russ
Well first off I wouldn't evaluate paste for a wave process. I would use solder bar instead. Flux - top side fillets and no shorting on the solder side, does it clean well after processing if using water soluble flux. How wide is the process win
Electronics Forum | Mon Dec 02 18:01:12 EST 2002 | GSW
Hi, Try to check if there is water absorbed in the flux or the humidity around the wave area. possibly plating on barrels that might be damaged?
Electronics Forum | Thu Aug 18 13:11:39 EDT 2005 | jsloot
We have our board house apply a peel coat mask that can be brushed off after wave or reflow. You need to brush off while it's still warm.
Electronics Forum | Mon Dec 02 12:52:40 EST 2002 | slthomas
We're trying a selective soldering pallet for the first time with mixed reviews. Are solder balls a prevalent problem with this process? Most of them seem to correspond with pallet wall locations....is it too much turbulence from the rotary chip wav
Electronics Forum | Mon Dec 02 16:01:15 EST 2002 | russ
If you can, attach athermocouple to the locations where you are getting solder balls. A previous product I had showed the same thing and we found that we had inadequate preheat leaving the liquid flux to splatter when it hit the wave. It could aslo
Electronics Forum | Tue Aug 09 10:01:26 EDT 2005 | pr
We have some large plated through holes, that we protect with hand placed Kapton dots before they go into the wave. Is there a better option? We are going to see if the boardhouse can put them on for us but I was curious how others are/would do this.