Electronics Forum | Thu Dec 01 14:24:25 EST 2005 | Amol Kane
Hi, I am having a SAC 305 solder paste with water soluble flux wetting issue. during reflow, the solder melts, but doesnt flow. the reflow profile was developed by the solder company person (Kester). the board is a test assembly to validate our LF pr
Electronics Forum | Fri Jul 13 10:57:04 EDT 2007 | dboudreau
Dear all, we are using the lead-free SN100C solder alloy for wave soldering. We are experiencing wetting problems each time we have to solder a thick board or a board with a large ground plane.I think that maybe we are not using the right flux. I w
Electronics Forum | Fri Apr 09 09:08:40 EDT 2010 | cast2010
Hello, I produce two types of board. - 100% Thru Hole - 50% thru hole and 50% SMT For the second, I have a bad wetting after the reflow on the top. The pcb board have Au-Ni pad. I use a water soluble paste. I clean the board with a solution with
Electronics Forum | Mon Sep 13 22:32:41 EDT 2010 | genesan
Hi all good morning and need advice from expertise here. One of my customer complain that they have constantly issues with one of their product and ask us to do cross section.The report show there was “no wetting to the PCB copper pad” and cause the
Electronics Forum | Mon Sep 13 22:58:49 EDT 2010 | genesan
Hi all good morning and need advice from expertise here. One of my customer complain that they have constantly issues with one of their product and ask us to do cross section.The report show there was “no wetting to the PCB copper pad” and cause the
Electronics Forum | Fri Sep 17 03:03:29 EDT 2010 | grahamcooper22
Hi Gani, looking at the HASL icture and the poor wetting of the solder over the pads I would imagine that the HASL coating is very thin on the pads and in actual fact isn't 'solder' but is tin /copper intemetallic and this has poor solderability. It
Electronics Forum | Mon Jan 29 12:42:24 EST 2001 | davef
Several points about your query are: * TI�s solderability protection specification is a minimum of 3 u" of palladium over 40-60 u" of nickel plate over a http://www.ti.com/sc/docs/products/logic/package/palladm/index.htm
Electronics Forum | Tue Apr 17 21:19:31 EDT 2001 | davef
Curious. Tell us more about: * Murata solderability protection * Solderability protection on the caps used to replace the Muratas * Reflow profile used with each of the two pastes * Differences in the two pastes
Electronics Forum | Tue Jul 30 10:04:51 EDT 2002 | dason_c
Dave, I am very interesting to know about the dewetting or pull back, we are currently use the uP78 paste. Will nitrogen, profile setting help to reduce the dewetting. Thank.
Electronics Forum | Thu Apr 22 21:34:58 EDT 2004 | adam
Thanks guys. I am from a subcon, we can't change the solder paste supplier and there is only one approved vendor for this component. I think I will try on the component solderability. Regards