Electronics Forum | Wed Sep 01 08:27:38 EDT 2004 | davef
Zinc from the brass [Cu3Zn2] diffuses into the tin causing solderability problems. Just 0.001% of Zn in your solder can render it fit for the scrap heap. So, you need a barrier plate between the brass and the tin. Copper or nickel-plating is commonl
Electronics Forum | Fri Feb 11 18:51:16 EST 2005 | primus
The operators use SET SEQ and SET SEG. I know all about getting these wrong, because if you forget the "Q" or the "G" you get SET SE which is SET SENSOR. That REALLY messes up our BEC! But then again, I believe our BECs are all calibrated wrong anywa
Electronics Forum | Wed Feb 22 08:31:42 EST 2006 | davef
Q1 Are there any standard regulating the subject? Very few infos found on IPC. A1 We�re unaware of standards for packing and storage for most types of boards. * IPC 4553 standard for Immersion Silver Finish, 3.8 Packing and Storage. * J-STD-033 and E
Electronics Forum | Thu Jun 08 07:31:14 EDT 2006 | slaine
Saw this and thought you may find it amusing. How many forum members does it take to change a light bulb? 1 to change the light bulb and to post that the light bulb has been changed 14 to share similar experiences of changing light bulbs and how t
Electronics Forum | Fri Dec 08 21:26:44 EST 2006 | billwestiet
You already have some good answers. A chemical isolation zone for RMA is a good idea. If you are looking for new see the two references you have and Austin America. If you are looking for used, see us at http://www.ietechnology.net. We presently
Electronics Forum | Thu Mar 29 20:15:41 EDT 2007 | darby
PCB > Origin > Origin 0 4 Teach the corner of the pcb at the mechanical stop. This data is from the machine origin. For a unit with a teach camera it will probably be around -25x, 95y. For a beam sensor around 70x, 28y. This is for a right to left
Electronics Forum | Fri Apr 20 14:02:26 EDT 2007 | JJ
RA, First, define "medium scale budget". Aside from that, I have used many systems, listed in my order of preference: 1. SRT1100 - superior board support - very reliable 2. ERSA IR550A - unique flexability due to infrared heaters 3. Metcal APR5000 -
Electronics Forum | Fri Jun 15 13:43:48 EDT 2007 | realchunks
I do want to run a profile, but they won't give > up the machine long enough for me to run one. > The boards that we are running through the wave > are large boards, with large caps, and large > transformers on it. We're building highend power
Electronics Forum | Sat Aug 25 08:39:15 EDT 2007 | gsala
If plastic Carrier Tape (CT)/ emboss tape, is made by: a)Polycarbonate material, it can withstand temperature around 120C� or may be more mantaining original dimension. b)Polystirene material, at max 45�C-50C� the CT starts to change dimensions and
Electronics Forum | Fri Nov 30 18:22:40 EST 2007 | mika
Hi Paul M, There are no silly questions but silly answers.. and here is maybe a few if I understand you correctly: If you consider place anything less than a 1.27mm (50mil) pitch component down or a chip less than a 1210, hey it maybe don't even work