Electronics Forum | Sun Aug 29 19:17:34 EDT 2004 | aqueous
Chen, It is always best to place one�s effort on determining the cause and content of the residue rather than trying to work around it. The first thing you must determine is the nature of the residue. Is it flux? In many instances, the residue is
Electronics Forum | Mon Jun 19 09:47:23 EDT 2017 | georgetruitt
You have a lot to think about! What does the flux manufacturer recommend as far as specifics like water temp or pressure? Do they recommend high temp di-water a detergent or saponifier? Do you currently have a cleaning machine, batch cleaner or inl
Electronics Forum | Mon Jul 12 11:35:27 EDT 2004 | Pierre RICHARD
Here are some answers to my questions after a good research. I also added more definitions that could help understand this esoteric language used in assembly, specially surrounding fluxes and their use. In blue italics are comments and extracts from
Electronics Forum | Tue Jan 05 20:29:32 EST 1999 | Steve Gregory
| A question for you all! | | Back in the good old days, we didn't always know how clean was clean. Much has changed. Much hasn't. | | My question concerns cleaning under, through, and around tight spaces. Way back when, we could not clean under 20
Electronics Forum | Wed Jan 06 09:55:22 EST 1999 | Chrys
| | A question for you all! | | | | Back in the good old days, we didn't always know how clean was clean. Much has changed. Much hasn't. | | | | My question concerns cleaning under, through, and around tight spaces. Way back when, we could not clea
Electronics Forum | Tue Oct 12 17:24:27 EDT 1999 | Kevin Ham
| | A question for you all! | | | | Back in the good old days, we didn't always know how clean was clean. Much has changed. Much hasn't. | | | | My question concerns cleaning under, through, and around tight spaces. Way back when, we could not clea
Electronics Forum | Thu Oct 28 11:50:11 EDT 2010 | phase1
We are having a little trouble with what appears to be a crystalization between our fine pitch parts. The problem appears after a a thourough wash of the pcb when dry. It looks like lead wiskers/haze between the joints.We are using water soluable lea
Electronics Forum | Fri Dec 08 21:26:44 EST 2006 | billwestiet
You already have some good answers. A chemical isolation zone for RMA is a good idea. If you are looking for new see the two references you have and Austin America. If you are looking for used, see us at http://www.ietechnology.net. We presently
Electronics Forum | Wed Jan 06 04:51:16 EST 1999 | Earl Moon
| | A question for you all! | | | | Back in the good old days, we didn't always know how clean was clean. Much has changed. Much hasn't. | | | | My question concerns cleaning under, through, and around tight spaces. Way back when, we could not clea
Electronics Forum | Tue Oct 12 17:40:01 EDT 1999 | Brian W.
| | | A question for you all! | | | | | | Back in the good old days, we didn't always know how clean was clean. Much has changed. Much hasn't. | | | | | | My question concerns cleaning under, through, and around tight spaces. Way back when, we coul