Electronics Forum | Thu Jun 24 11:41:10 EDT 1999 | John Thorup
| Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody hel
Electronics Forum | Thu Sep 04 03:26:18 EDT 2014 | eurekadrytech
Hi all: Interesting question you have raised as it concerns the rate of absorption by the board material. I represent http://www.EurekaDrytech.com and could assist in resolving the blistering problems you're facing. First some questions. 1. Is the
Electronics Forum | Thu Jun 24 12:43:08 EDT 1999 | Earl Moon
| | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody h
Electronics Forum | Fri Jun 25 01:11:31 EDT 1999 | Vinesh Gandhi
| | | Recently, there has been an upsurge in the Pin Hole/Blow Hole problem in our wave soldering process. We are baking the PCBs for 2 Hrs. at 125 degree C. The Wave Soldering profile seems to be O.K. Still the problem is persistent. Can somebody
Electronics Forum | Mon Aug 18 15:04:25 EDT 2014 | rgduval
Off hand, I can't recall a "formula" for how long boards could sit in a specific RH environment. I've done a couple of quick Google searches, and can find a bunch of information on the dispersion rate of moisture in various PCB materials, but, nothi
Electronics Forum | Sun Sep 07 20:51:52 EDT 2014 | natashakt
1. Is the high RH environment consistently at 72% RH and 21.4 degrees Celsius? No, over the past 2 weeks I have recorded the highest at the moment: 67% RH at 22.6 degrees C and lowest (it is Spring not summer yet): 31.9% RH at 19.0 degrees C. Or d
Electronics Forum | Sat Jan 10 09:04:47 EST 2015 | jandon
class 3 requires 100% barrel fill Class 3 requires 75% vertical fill of solder for component with less or more than 14 leads. Not 100% fill.
Electronics Forum | Tue Jan 05 20:29:32 EST 1999 | Steve Gregory
| A question for you all! | | Back in the good old days, we didn't always know how clean was clean. Much has changed. Much hasn't. | | My question concerns cleaning under, through, and around tight spaces. Way back when, we could not clean under 20
Electronics Forum | Wed Jan 06 09:55:22 EST 1999 | Chrys
| | A question for you all! | | | | Back in the good old days, we didn't always know how clean was clean. Much has changed. Much hasn't. | | | | My question concerns cleaning under, through, and around tight spaces. Way back when, we could not clea
Electronics Forum | Tue Oct 12 17:24:27 EDT 1999 | Kevin Ham
| | A question for you all! | | | | Back in the good old days, we didn't always know how clean was clean. Much has changed. Much hasn't. | | | | My question concerns cleaning under, through, and around tight spaces. Way back when, we could not clea