There are some common reason for capacitor cracking on my web page if you want to have a look. The document can be downloaded for your reference. | Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior
Electronics Forum | Mon Jun 08 15:29:17 EDT 1998 | Gary Simbulan
| Earl, et al, | Boy things get old and cold around here fast. I promised more detail on my capactior problem and I thought I could drop something completely different in the same message and tell a tale of solder balls. | First the caps. We stil
Electronics Forum | Tue Aug 31 17:36:36 EDT 2004 | davef
NO-LEAD COMPONENTS WITH LEAD SOLDER ISSUE: We agree with Russ. We've dicussed this several times on SMTnet. For instance, look here http://www.smtnet.com/forums/Index.cfm?CFApp=1&Message_ID=25394 LEAD COMPONENTS WITH NO-LEAD SOLDER ISSUE: We disa
Electronics Forum | Fri Jan 22 15:48:14 EST 1999 | Chrys
| Hello, | | I will be evaluating and qualifying two equipment types. The first is a fountain soldering device. I need practical advice on all the stuff you guys and gals know about as good, bad, ugly, best applications, setup, limitations, and all
Electronics Forum | Wed Aug 18 21:10:23 EDT 1999 | se
| | | Hi, | | | I'd like to ask some tips about the merits and shortcomings o | | | of both screen printer and stencil printer. For small quantity and highly mixed usage, which type of printer is suitable to our | | | application? | | | The board
Electronics Forum | Tue Jun 01 17:37:34 EDT 2004 | lynnmc
Any view on what the minimum reflow temperature is for a SAC ball bga to form a reliable joint with PbSn solder?
Electronics Forum | Mon May 16 22:59:40 EDT 2005 | davef
We believe your problem is caused by the mismatch in CTE of the material ised in your BGA. In fact, this "potato chipping" [where the corners curl-up] is present in all BGA. The issue is the matter of degree. [Mismatching CTE is how old thermostats
Electronics Forum | Tue Jun 01 19:23:15 EDT 2004 | Ken
profile it for the tin/lead paste. The tin in the solder paste will begin to disolve the sac ball. This is exactly the same scenario as 90/10 (80/20)high temp balls found on ceramic bga and many super bga devices (except the sac balls are now tin r
Electronics Forum | Wed Feb 01 06:02:59 EST 2006 | joe
Hi, SAC BGA's in a SnPb reflow process can be achieved by ensuring the temp. on the BGA is at a peak min of 220�C and a time above 207-210�C for 60 - 90 Sec. Lower temperatures have shown incomplete mixing of alloys and some voiding.
Electronics Forum | Wed Apr 30 12:26:10 EDT 2008 | dphilbrick
There must be discussions about this on SMTnet but I have yet to find them. I would like to hear from all you smart people about running LF and PB BGA�s on the same board using 63/37 solder. If you run your profile up to peak at around 225C +/- (nitr