Electronics Forum | Mon Nov 27 08:05:50 EST 2006 | davef
There is no standard for a strain gage measurement of allowable deflection of a board or a fixture. It's possible that your fixture is causing the BGA cracking that you see. What protion of the BGA is cracking? If it is the solder connection, sear
Electronics Forum | Fri Mar 24 12:16:37 EST 2006 | patrickbruneel
Darn Rob you're brilliant You just solved the dilemma of micro cracks and hot tear in lead free, just add a softer metal like.....and the joints won't crack. You wrote "BTW: Lead is far softer & dissolves far more easily than copper or tin, hence wh
Electronics Forum | Sat Nov 25 21:26:55 EST 2006 | callckq
Dear all, I have an issue here where we found BGA crack. Understand from friend, we need to study any possiblity of our own jig or fixture cause this problem via strain gauge measurement..My question: Is there any standard @ specification establish
Electronics Forum | Sat Oct 03 07:26:01 EDT 2009 | cflames17
Check the reference plate on the hydra to make sure it is not cracked or delaminated. I have had problems with the glue coming loose and the plate flapping causing this same problem. check hydra camera calibrations, this to may help.
Electronics Forum | Fri Feb 26 12:01:08 EST 2010 | jdumont
Hey its probably the silicone adhesive
Electronics Forum | Mon Mar 01 07:24:55 EST 2010 | jdumont
No problem just busting, trying to keep the mood light! Cheers
Electronics Forum | Thu Jul 15 16:22:22 EDT 2010 | wrongway
If you found one for that price would you realy trust that it would be as good as you would need it to be
Electronics Forum | Sun Apr 16 14:37:25 EDT 2000 | Roberto Navarro
Hi, I work for Nortel and here rework BGA'S we use DRS22 rework station and CRT 2000 X-ray inspection. The main problem is put again the BGA on the PCB because you need reboling the PCB and you could damage the soldermask. Talking about Air-vac is ve
Electronics Forum | Fri Mar 24 13:25:24 EST 2006 | patrickbruneel
See Samir that's what happens if you go too lead-free seminars, they feed you crap. If they served you lunch with bismuth chips its time you see a doctor or you end up like WML. By the way any takers?? Who in this forum volunteers to be the first to
Electronics Forum | Tue Feb 23 13:49:20 EST 2010 | davef
There should be no problem. Recognize that the residue of some low residue fluxes turn a milky-white color when you wash them. This could freak your quality people.