Electronics Forum | Wed Nov 12 17:35:54 EST 2003 | jseagle
There is also McDry storage cabinets offered through Seika Machinery. www.seikausa.com
Electronics Forum | Wed Jan 04 16:21:14 EST 2006 | jrlouden
What is the preferred method of under stencil wiping? (Wet or Dry wipe)
Electronics Forum | Tue Feb 07 05:40:16 EST 2006 | pavel_murtishev
Good day, J-STD-033A: 4.1.2.2 Moisture Sensitivity Levels 5-5a For moisture sensitivity Levels 5 and 5a with floor life exposure not greater than 8 hours, a minimum desiccating period of 10X the exposure time is required to dry the SMD packages en
Electronics Forum | Wed Aug 02 16:47:44 EDT 2006 | Merle
Should drying be done after aqueous wash? If so, how long and at what temperature?
Electronics Forum | Mon Oct 04 10:02:09 EDT 2010 | babe7362000
I have a question about Drying a PCB after it goes thru the washer. Just wondering if others have to dry components off using air at the end of the wash? Our current process is that we wash the boards and dry certain parts off with the air hose aft
Electronics Forum | Wed Jun 22 09:50:53 EDT 2011 | mosborne1
McDry - don't even waste your time with anyone else..
Electronics Forum | Fri Jun 24 12:29:40 EDT 2011 | deanm
Manoel, No, we do not use Totech dry boxes. Just another name to consider.
Electronics Forum | Wed Feb 21 20:00:09 EST 2001 | davef
Sounds like you received some good advice. Most of our stencils are used once a day [at most], so more often than not they are air dried. If we goof-up and need to reuse a stencil during a day when we have limited drying capacity, we wipe the lowes
Electronics Forum | Mon Aug 31 13:04:13 EDT 2009 | bandjwet
We have tried air drying (using shop air) our SMT stencil post sonic cleaning. This technique only "pushes" the water droplet around to the other side of the stencil. Air drying causes the "Invar" stencils to rust as the water sits on the stencil sur
Electronics Forum | Wed Jun 22 01:57:28 EDT 2016 | sachinverma
we face the problem to last month dry solder issue.when we found PCB is dry. (PTH not fill not properly)then we change the parameter like flux Tank pressure increase 130 to 250. after these activity PCB is ok no dry solder found......but problem is o