Electronics Forum | Tue Aug 10 07:47:12 EDT 1999 | Brian
| | | hello to everybody, | | | we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; | | | does anybody know how to eliminate flux residues or how not to produce them during rew
Electronics Forum | Thu Mar 09 20:48:30 EST 2000 | Dave F
Van Hoang: Welcome to SMTnet!!!! Regarding your problems: 1. Cleaning glue: Check the SMTnet archives. For instance, a recent thread was: cleaning glue off of stencils - pr 13:41:43 03/03/2000 2. Bridging on the wave: Bridging on the wave h
Electronics Forum | Thu Mar 09 20:48:30 EST 2000 | Dave F
Van Hoang: Welcome to SMTnet!!!! Regarding your problems: 1. Cleaning glue: Check the SMTnet archives. For instance, a recent thread was: cleaning glue off of stencils - pr 13:41:43 03/03/2000 2. Bridging on the wave: Bridging on the wave h
Electronics Forum | Mon Aug 09 10:10:29 EDT 1999 | Gian.D
hello to everybody, we have a really satisfactory no clean process, both smt/reflow and wave soldering, but we get troubles with defects rework; does anybody know how to eliminate flux residues or how not to produce them during rework operations? Th
Electronics Forum | Tue Dec 07 17:40:30 EST 2004 | davef
We'd suggest listening to your CSP component supplier. The standoff is too low. Check with your flux suppliers for the information you seek.
Electronics Forum | Mon Dec 13 16:25:37 EST 2004 | saragorcos
Hi Scott - No clean assemblies have a very low tolerance for processing residues, and long term reliability is compromised if residues from incoming bare boards, components, or un-solublized flux residues are not dealt with. It is critical to contro
Electronics Forum | Mon Oct 22 11:47:59 EDT 2007 | brulal1
Thank you guys for your help, I do not clean any on my assemblies who are build by the SMT an wave soldering department, we do used liquid fluxes Kester 951 and cored wire keester 245, usually it�s for batteries connector, led, terminal and wire rap
Electronics Forum | Thu Jan 16 15:55:31 EST 2003 | MA/NY DDave
Hi I have a funny feeling that Mike Konrad and I know each other from IBM-Endicott days, yet I could be wrong. It would be funny?? Mike gave a good answer. The Rosin or Rosin Mildly Activated Flux (RMA) if on the board at ICT (In Circuit Test) wil
Electronics Forum | Fri Jun 19 18:44:23 EDT 1998 | Steve
Does anyone have wave solder experience using OSP and VOC free no clean flux?
Electronics Forum | Mon Jul 01 22:24:10 EDT 2002 | Por
Thanks for your advise Normally, We do not add any liquid flux (clean or No-clean) during touch up process but this case is an error. Lonco 23F is Nc flux. but our board is clean. However, there are 6 boards that found the white residue and our