Electronics Forum | Mon Jan 07 21:07:00 EST 2002 | davef
Using a flux pen sounds like a good idea. Comments are: * I assume you�re talking aqueous flux. If not, some NC flux pens leave white residues. Nearly all of 15 samples suffered to varying degrees with white residues. * Use the same flux that you
Electronics Forum | Tue Jun 08 12:49:41 EDT 1999 | Dave F
| Hi,my master | How to iron out such soldering bridge with below conditions: | 1.The component(Harness)lead pitch is 2.0mm,the lead length is 3.2mm. | 2.PCB width is 1.6mm.Pad size is 1.65mm.Its a single copper PCB | 3.using spraying fluxer and n
Electronics Forum | Tue Jun 08 13:06:53 EDT 1999 | Kevin Hussey
| | Hi,my master | | How to iron out such soldering bridge with below conditions: | | 1.The component(Harness)lead pitch is 2.0mm,the lead length is 3.2mm. | | 2.PCB width is 1.6mm.Pad size is 1.65mm.Its a single copper PCB | | 3.using spraying fl
Electronics Forum | Tue Jun 08 17:52:53 EDT 1999 | Chrys Shea
| | | Hi,my master | | | How to iron out such soldering bridge with below conditions: | | | 1.The component(Harness)lead pitch is 2.0mm,the lead length is 3.2mm. | | | 2.PCB width is 1.6mm.Pad size is 1.65mm.Its a single copper PCB | | | 3.using s
Electronics Forum | Mon Oct 22 16:47:09 EDT 2012 | edmundo
We use a NC Flux in the wave solder and after aAcelerated Life Test cicle we found contamination white residues paths between some solder points. Does somebody know a possible cause for this contamination.
Electronics Forum | Tue Oct 23 12:24:47 EDT 2012 | edmundo
thank you for the information .We are planning to send the units for analysis.
Electronics Forum | Mon Mar 07 16:12:02 EST 2022 | chris007
This is recommended by our EMS to make sure flux is not cheating AOI.
Electronics Forum | Wed Jun 17 16:19:10 EDT 1998 | Ryan Jennens
| We are facing a problem of high contamination on boards after wave soldering. We want the contamination to be under 24 ugm/inch square. We are using a no clean flux with the spray fluxer unit of wave soldering. The contamination is higher on the e
Electronics Forum | Tue Oct 23 10:41:36 EDT 2012 | blnorman
Ideally first you need to analyze the residue to see what it is. We had a customer with white residues after wave and elemental analysis revealed tin.
Electronics Forum | Tue Apr 02 14:24:35 EDT 2013 | hegemon
Too many hands in the bucket, unless the owner is one of the engineers. Typically flux is not rated or classified by "feel". What are you soldering? Wires? Components to PCB? What is your cleaning capability or requirement? Aqueous? No-Clean? Ul