Electronics Forum | Wed Sep 01 08:27:38 EDT 2004 | davef
Zinc from the brass [Cu3Zn2] diffuses into the tin causing solderability problems. Just 0.001% of Zn in your solder can render it fit for the scrap heap. So, you need a barrier plate between the brass and the tin. Copper or nickel-plating is commonl
Electronics Forum | Fri Sep 21 10:35:37 EDT 2012 | davef
Flash gold is just thin electrolytic gold plating over electroless nickel or electrolytic nickel. Flash gold plating ... * Less than 3 microinch thick will be porous and take solder poorly * Greater than 10 microinch thick will cause brittle solder c
Electronics Forum | Tue May 13 06:57:10 EDT 2003 | davef
Your vendor site is totally correct. 2Ag is an excellent solder, but it does nothing to prevent tin and gold from reacting chemically. An earlier poster is correct gold goes into solution in liquid solder very fast, less than a second. Gold and ti
Electronics Forum | Mon Feb 09 16:55:28 EST 2009 | cuperpeter
Hi Sachin, thanks for your feedback. According to our supplier, surface plating is electrolytic gold over Nickel(not ENIG), but I think that is a still improper thickness for Au. (according to 3rd Working Draft from September 2008 of IPC 2221B "0.4
Electronics Forum | Tue Mar 31 05:26:14 EDT 2009 | d0min0
Hello, we had similar problem in the past - when we had to change PCB supplier from a batch of hundreds of boards (NiAu plated, SnPb process) we got 2-3 boards with paste wicking to components leads what we did, was to check the thickness of gold on
Electronics Forum | Tue Jul 15 16:30:57 EDT 2008 | boardhouse
Hi Aj, Recommended Immersion gold thickness would be 3-5 Micro inches over 140 -200 micro inches of Nickel. Thicker Immersion gold than 5 micro inches can cause solder joint embrittlement. Gold readily dissolves in molten solder and will be present
Electronics Forum | Thu Jul 10 09:16:41 EDT 2008 | aj
Hi all, What should the typical gold thickness be on ENIG boards ? aj...
Electronics Forum | Wed Feb 04 06:26:20 EST 2009 | sachu_70
Hi Peter, The defect you observe during the second side reflow could be caused due to improper Au plating thickness in the PCB fabrication process. You can refer IPC-2221 wherein plating thicknes for ENIG mentions 0.08um to 0.23um for Immersion Gold,
Electronics Forum | Mon Jul 28 06:23:29 EDT 2008 | cobar
Please look up http://www.shanelo.co.za/Black%20Pad%20Index.htm and check out the article named"Soldering to gold a practical guide."
Electronics Forum | Mon Dec 22 16:09:02 EST 1997 | Justin Medernach
| I am designing an SMT pad for a ss metal switch. | Finished copper thickness is .0014 and nickle-plating | originally is 150 millionths. Initial testing yields 100,000 to 150,000 switches before intermitent failures (copper is reached.) I want 50