Electronics Forum | Tue Dec 17 08:38:30 EST 2002 | Randy Villeneuve
Jim, In most cases if you can eliminate a process you will save money. With that in mind, an all surface mount or all through hole design is prefered. There are alternatives to that rule, like hybrid designs that can be pin and paste soldered. It al
Electronics Forum | Tue Aug 26 17:02:10 EDT 2008 | allwave
What brand of flux and wave solder machine are you using? George
Electronics Forum | Mon Dec 02 17:02:28 EST 2002 | Vince Whipple
Steve, I agree with the recommendation to check the temperature. This is the first place to go. Is this an IPA or water based Noclean? What is the topside temp of the assembly at the effected areas? If you are too cold you will have a tendency to hav
Electronics Forum | Wed Dec 04 09:24:52 EST 2002 | jseagle
I have found that preheating the solder pallets prior to use helps cut down on the solder balling. Also, we do not cool the pallets between passes and we use a spray fluxer because a hot pallet will knock down the head on a foam fluxer. We use WS f
Electronics Forum | Tue Aug 09 12:12:57 EDT 2005 | davef
Why are you placing Kapton dots on your board prior to wave soldering? * Prevent solder from touching the hole and the area around it. [If so, why do you need to do this?] * Prevent solder from flowing up through the hole and coating portions of the
Electronics Forum | Tue Aug 09 13:51:03 EDT 2005 | patrickbruneel
You can also insert a stainless steel screw the size of the hole in the board before wave soldering, this will prevent the solder from wicking up to the top or close the hole (this is real cheap). I still remember the good old days using toothpicks t
Electronics Forum | Mon Dec 02 13:16:31 EST 2002 | kenBliss
Hi Steve The people who will have the answer is the experts at EMC Global Technologies. They know their stuff, they are the leader in the solder pallet industry. They design and build them to work right. http://www.emcgti.com for contact info. Hop
Electronics Forum | Thu Dec 05 11:36:30 EST 2002 | William Guatemala
Have you check the flux gravity lately? If not, Check the flux gravity every 6 hours to make sure proper parameters are meet. Here is a list of things that may cause your solder ball problems; Excecive heat, defective fixtures, preheating temperature
Electronics Forum | Wed Jul 27 15:54:44 EDT 2005 | Hiram
Hi everybody, We have wave solder fixtures made of Durapol and multiple wave solder machines. Most likely we�ll use the same pallets for either tin-lead or lead-free solder for a while (of course after washing the pallets). Should we test the palle
Electronics Forum | Fri Feb 09 02:30:50 EST 2007 | Muhammad Haris
What are Resins, Solvents, Activators, and Thickening Agents in Solder Paste and what are their helpful and harmful effects? AND What are the purposes/properties and effects of Sn(Tin), Pb(Lead), Ag(Silver), Bi(Bismuth), In(Indium), Cu(Copper), Ni(