Electronics Forum | Tue Jan 04 10:40:41 EST 2011 | johanhuizing
Hello Piter, I don't know which type of HASL we will be using, we decided to do some test and I have to decide together with two other people which material we will try. Searching on the internet i discovered that it's not so easy to find a good sol
Electronics Forum | Sat Dec 30 04:23:50 EST 2023 | 012band
I have used LTS (Sn57.6%Bi0.4%Ag) solder balls for soldering on Ni/Au pads, and I have observed a wrinkle pattern on the ball surface. When you attempted soldering on CuOSP substrate pads under the same conditions, the surface appeared normal. Additi
Electronics Forum | Fri Oct 29 10:02:28 EDT 1999 | John Thorup
Chris A lot of people have reported sudden, fab lot related problems with Ni/Au pads. These are usually characterized by a discoloration of the gold and called cheerful names like "black pad disease". This can be a process problem at your fab house
Electronics Forum | Tue Mar 14 07:59:41 EST 2000 | JAX
Emmanuel, The discussion on what finish to use whether it be HASL, Immersion gold over nickel, Organic Solderability Preservatives, ect...... is still ongoing. This is not the only decision you need to make. Do you plan on Soldermask Defined Pads? Wh
Electronics Forum | Wed Dec 13 10:24:52 EST 2000 | Wolfgang Busko
Hi Jack, I once tried this finish ( without changing any process parameters ) and encountered wetting problems even in the first reflow process. It was thought as cheaper alternative to Ni/Au we use for planarity reasons. Heard of the same problems
Electronics Forum | Mon Apr 17 16:17:47 EDT 2000 | Dennis Fall
Typically, Sn/Pb solders are used to preserve solderability on leaded and leadless SMT components. Are other finishes (such as those used in PCB manufacturing e.g. Sn, NiAu, OSP's, etc.) frowned upon by PCB stuffers and their customers? I am intere
Electronics Forum | Tue Mar 14 07:59:41 EST 2000 | JAX
Emmanuel, The discussion on what finish to use whether it be HASL, Immersion gold over nickel, Organic Solderability Preservatives, ect...... is still ongoing. This is not the only decision you need to make. Do you plan on Soldermask Defined Pads? Wh
Electronics Forum | Fri Jul 16 13:33:31 EDT 1999 | Dale
We are converting from COB to SMT on a product line and want to optomize the PCB as far as Laminate, plating, passivation etc. This is a high temp application 150C. We are presently using BT Laminate but would like to get away from this. We are lo
Electronics Forum | Fri Jul 16 22:44:27 EDT 1999 | Vic Lau
| We are currently assemblying several different board type with gold plated lands with varying results. Can any of you that has successful experience in this area give me some pointers. What paste do you use? Do you use the recommended reflow pro
Electronics Forum | Tue Oct 23 09:09:27 EDT 2001 | Cemal Basaran
What is the reflow temperature you use to attach this package to your PCB.? I did extensive study on this package and compared it with other packages. I used our own Moire Interferometry, SEM, EDX studies. In my opinion the problem is TI does not man