Electronics Forum | Wed Aug 26 03:21:00 EDT 2009 | sergey2007
Hi Graham, the MSD level of the component is 3. I am not sure that my customer properly stored the component before the soldering process. And I am not sure that it was dried at all. The customer says they did everything that they had to, but I just
Electronics Forum | Mon Nov 12 19:02:48 EST 2012 | jmartens1978
My first attempt was similiar to that. It was a straight ground trace running past the circular pads that were recieving the shocks. It was hit and miss when the arcs would occur. When I cut notches in the trace so the ground line had a point next to
Electronics Forum | Thu Jun 24 23:52:36 EDT 1999 | Dean
| | | Dear guys, | | | | | | I have some problem on assembling micro-BGA with solder paste (63/37). The micro-BGA we assmeble is 0.75mm pitch and with 45 pin (solder bump is 96.5/3.5Ag). The stencil is a laser-cut stencil with 5 mil thickness. We
Electronics Forum | Thu Aug 20 08:23:23 EDT 2009 | ratsalad
One diagnostic tool that I have found useful in the past is the "hot plate test". Place suspect components and/or PCB's on a hot plate and turn it on High. Then observe. Granted the conditions on the hot plate are not the same as in a reflow oven,
Electronics Forum | Mon Jun 28 11:51:36 EDT 1999 | Brian Wycoff
| | | | Dear guys, | | | | | | | | I have some problem on assembling micro-BGA with solder paste (63/37). The micro-BGA we assmeble is 0.75mm pitch and with 45 pin (solder bump is 96.5/3.5Ag). The stencil is a laser-cut stencil with 5 mil thicknes
Electronics Forum | Fri Sep 08 03:37:54 EDT 2017 | m_imtiaz
there any problem if Lead Free finish PCB being process using Leaded Solder Paste...? It is totally related to the manufacturing process and quality of joint, not to any specific compliance issues related to the European Union, China or any. Regards
Electronics Forum | Thu Oct 11 22:25:50 EDT 2001 | davef
Bruce I�m with yall. Designers and fabricators say �pins�. You say: * BGA pins are 1mm [0.039�] pitch. * BGA pads are 0.4mm [0.0157�] diameter. * BGA pins are 0.6 mm [0.024�] side-to-side. * Board thickness is ~0.4 mm [0.015�] First, as you can
Electronics Forum | Fri Mar 07 15:20:11 EST 2003 | davef
O'Connor: IPC-A-610, section 12.4.4 SMT Soldering Anomolies - Nonwetting was added primarily to accomidate OSP boards. Heated flux is used to remove the 'lacguer'. So, you end-up with a copper colored border [or shadow] around the pads, where there
Electronics Forum | Mon Oct 19 15:08:14 EDT 2009 | markhoch
Would be glad to offer some assistance, but I've got a couple of questions first: 1) What type of supplemental flux are you using? (If any) 2) Is your problem consistent across all assemblers, or can you trace the assemblies with solder ball issues b
Electronics Forum | Fri Dec 16 03:47:46 EST 2005 | gpaelmo
Anyone have problems wave soldering white tin finish? We are an ems and our customer provides us the pcb's. SMT and TH components on the board. SMT is fine but when we wave solder, wetting to top side is very poor (solder only flows half way up). We
Products, services, training & consulting for the assembly, rework & repair of electronic assemblies. BGA process experts. Manufacturers Rep, Distributor & Service Provider for Seamark/Zhuomao and Shuttle Star BGA Rework Stations.
Training Provider / Manufacturer's Representative / Equipment Dealer / Broker / Auctions / Consultant / Service Provider
1750 Mitchell Ave.
Oroville, CA USA
Phone: (888) 406-2830