Electronics Forum | Thu Jan 06 17:20:09 EST 2011 | dyoungquist
Check out this article about nitrogen and soldering: http://www.tequipment.net/pdf/Hakko/TN00000022.pdf
Electronics Forum | Thu Dec 21 12:46:19 EST 2017 | slthomas
Are the jobs so small and the setup time so high that it precludes running them on two or three machines?
Electronics Forum | Tue Dec 19 16:30:23 EST 2017 | charliedci
We have several selective soldering machines, that because of several minutes of process time per PCB, one operator can keep 2 or sometimes 3 machines loaded and running. Other days only 1 machine is running but operator does not have enough time to
Electronics Forum | Fri Dec 22 07:30:30 EST 2017 | stephendo
For me it looks like a sales issue. Having more operators would probably not help them meet their metric. If you cannot meet or defeat a metric, switch metrics. (said tongue in cheek)
Electronics Forum | Thu Dec 21 15:35:21 EST 2017 | emeto
For me it looks like a scheduling issue. You can do time studies on your assemblies and predict the best workload, based on scheduling the jobs in the right sequence. Also it sounds like you have only one operator. Train more people to operate will h
Electronics Forum | Thu Dec 21 15:13:16 EST 2017 | georgetruitt
Is the process the same for every product running through the selective solder machine? Load program, acquire or set up fixture, Change/load flux?, Change/Load solder pot? Are the machines cold when the operators need to use them or are the machin
Electronics Forum | Wed Dec 27 09:05:35 EST 2017 | charliedci
All the response is appreciated. We have 4 SS machines and 2 operators (normally). Some jobs take up to 15 minutes (multiple boards), some take less than 2 minutes (machine time). Some involve fixtures, preheat, some may require the operator to mon
Electronics Forum | Thu Jan 17 08:56:09 EST 2019 | babe7362000
Is there anyone on here that is currently using a RPS Selective Solder Machine? Rhythm SS ?
Electronics Forum | Wed Jul 30 16:16:19 EDT 2003 | swagner
What is the industry standard for wave and selective solder PPM defect rate for a world class facility, any responses are appreciated.
Electronics Forum | Mon Jan 15 08:54:40 EST 2024 | SMTA-64304553
Trying to understand the impact of iron contamination above IPC recommendations (0.02%) on selective solder joints. Brittleness and discolouration are known but are there other factors that should be accounted for?