Electronics Forum | Wed Sep 18 10:06:30 EDT 2002 | Bob M
I place 15-20 mil a lot. You need to look at your pad to apature reduction. Your stencil thickness. The type of paste your using. We use 2-5 mil reduction on each side as a general rule on fine pitch. This varies depending on pad width. We also use 5
Electronics Forum | Wed Sep 18 12:31:16 EDT 2002 | dragonslayr
My suggestion is to conduct a Design For Manufacturing (DFM)study on the assembly in question. Pay particular attention to the pad sizes, component lead dimensions and satisfy yourself that those two factors are correct. Given that pads match compone
Electronics Forum | Fri Jul 06 13:44:15 EDT 2007 | shrek
Krikies! seems like a head-scratcher if I may say so me-self. I would say the other ogre is right, that surface finish will play a big factor in your solder joint's grain structure or how shiney 'tis. Non-HASL bearing finishes will typicaly exhibit
Electronics Forum | Mon Jan 17 17:38:29 EST 2011 | bandjwet
All: I am reaching out to get some suggestions on the right flux to use as well as a recommended cleaning process for soldering a KOVAR RF shield using 80/20 Au/Sn solder to a ceramic hybrid. The recommended profile is 4-5 min at 280C and at least
Electronics Forum | Mon Apr 26 09:46:05 EDT 1999 | C.K.
Chrys: I have checked all the basic elements of Wave solder joint formation: fluxing, preheating, and lastly soldering. For checking the fluxer, i used a product from ECD that's very similar to what you desribed called the flux-o-meter. It did a
Electronics Forum | Fri Apr 20 15:27:00 EDT 2001 | jimlew
We do some aperture reductions - but it's not the 10% i'm accustomed to. Looks like it should be more than we currently do (I think we do 10% of length, but no width). Don't think we have a slumping problem, and we're not doing snap-off, only contact
Electronics Forum | Mon Apr 19 20:49:13 EDT 1999 | Dave F
| Netters, | | When I reflow a PCB there is a discoloration of silkscreen and mask. It appears if Profile is too hot! But I dont think so, maybe I'm wrong? | | 1. Kester 293 no clean | 2. 2.1 C/s for 30s to 150 C | 3. .5 - .7 C/s for 60s to 185
Electronics Forum | Thu Sep 19 11:14:45 EDT 2002 | Jim M.
We had lots of problems with bridging on 15.8mm pitch, QFP17-160 at the start.The board was .032 thick, double sided-six boards to a panel. Here is the problems (not neccessarily in the biggest to little but as i remember them) and solutions that he
Electronics Forum | Tue Feb 27 11:03:09 EST 2007 | Marcin
Hi All, Anybody knows what is the minimum clearance between through hole component and chip component? Problem description: On bottom side of my pcb are only 0603 chip components mounted on glue. One of the component is located very close to hole
Electronics Forum | Thu Oct 17 17:18:48 EDT 2002 | Leandro G. Barajas
Hi everybody, This is a simple posting to initiate a discussion on different ways to troubleshoot, improve, and control the Stencil Printing Process SPP in SMT manufacturing. There are many SPC, ANOVA and other analysis techniques that provide insi