Electronics Forum | Mon Dec 17 11:55:08 EST 2007 | chef
I recently had the same problems, solder bridges on every thing I made, different customers boards, etc. I wave with no-clean flux. As I sorted out problems (pin holes, blow holes, splatter, etc.) I found a lot of variable factors. I changed flux,
Electronics Forum | Wed Mar 01 16:58:03 EST 2000 | Dave F
Robert: On your balls: Solder suppliers make several "standard balls" and can advise you. On your cleaner: Recycling water / direct to drain? Most batch cleaner suppliers can advise you on recycling and filtering systems to keep you out of troub
Electronics Forum | Wed Mar 01 16:58:03 EST 2000 | Dave F
Robert: On your balls: Solder suppliers make several "standard balls" and can advise you. On your cleaner: Recycling water / direct to drain? Most batch cleaner suppliers can advise you on recycling and filtering systems to keep you out of troub
Electronics Forum | Mon Dec 17 19:01:45 EST 2007 | bbarton
As someone with a LOT of experience with the "low cost" alternative alloys, primarily SACX, I have one simple question....Are these shorts a new phenomena? WAS your process in control, and all of a sudden it's not? If the answer is YES, take a look a
Electronics Forum | Wed Mar 01 10:46:26 EST 2000 | Robert Hartmann
Kelvin, Thanks for the help. The actual opening size is .440 mm, but I think what you said makes sense. After discussing with the customer, it looks like it is the height which matters, more than the diameter. We have learned that the height of t
Electronics Forum | Wed Mar 01 10:46:26 EST 2000 | Robert Hartmann
Kelvin, Thanks for the help. The actual opening size is .440 mm, but I think what you said makes sense. After discussing with the customer, it looks like it is the height which matters, more than the diameter. We have learned that the height of t
Electronics Forum | Tue Jul 31 09:12:03 EDT 2012 | solonmfg
test - Administrator please delete
Electronics Forum | Mon Jun 23 12:50:49 EDT 2003 | russ
There are coatings available for Stainless that will greatly retard the solder from wetting to/eating the metal. This may be a cheaper route to go than Using all Titanium. The coating is melonite QPQ (quench-polish-quench)I really don't have any mo
Electronics Forum | Thu Jan 21 09:27:33 EST 1999 | Earl Moon
Hello, I will be evaluating and qualifying two equipment types. The first is a fountain soldering device. I need practical advice on all the stuff you guys and gals know about as good, bad, ugly, best applications, setup, limitations, and all the re
Electronics Forum | Mon May 03 10:52:18 EDT 2010 | davef
We're not sure that such data is available. What guidelines does your flux supplier provide in soldering with this process?